Polyethylene composition and film having a good permeability, stiffness and sealability

ABSTRACT

A polyethylene composition includes a first polyethylene which is an ethylene copolymer having a weight average molecular weight of from 70,000 to 250,000 and a molecular weight distribution Mw/Mn of &lt;2.3, a second polyethylene which is an ethylene copolymer or homopolymer having a weight average molecular weight of from 15,000 to 100,000 and a molecular weight distribution Mw/Mn of &lt;2.3, and a third polyethylene which is an ethylene copolymer or homopolymer having a weight average molecular weight of from 70,000 to 250,000 and a molecular weight distribution Mw/Mn of &gt;2.3, where the first polyethylene has more short chain branching than the second polyethylene or the third polyethylene. The polyethylene composition has a soluble fraction in a CEF analysis of at least 10 weight percent. Film made from the polyethylene composition may have a machine direction 1% secant modulus of □190 MPa (at a film thickness of about 1 mil), a seal initiation temperature (SIT) of ≤100° C. (at a film thickness of about 2 mil), an area of hot tack window (AHTW) of ≥160 Newtons·C° (at a film thickness of about 2 mil) and an oxygen transmission rate (OTR) of ≥650 cm3 per 100 inch2 per day (at a film thickness of about 1 mil).

This application claims the benefit of the earlier filing date of Canadian Application Serial Number 3011038 filed on Jul. 11, 2018, which application is incorporated herein by reference in its entirety.

The present disclosure provides polyethylene compositions which when blown into film have good stiffness, good oxygen permeability and good sealability. The polyethylene compositions include two polyethylene components which are made with a single site polymerization catalyst and one polyethylene component which is made with multi-site polymerization catalysts.

Multicomponent polyethylene compositions are well known in the art. One method to access multicomponent polyethylene compositions is to use two or more distinct polymerization catalysts in one or more polymerization reactors. For example, the use of single site and Ziegler-Natta type polymerization catalysts in at least two distinct solution polymerization reactors is known. Such reactors may be configured in series or in parallel.

Solution polymerization processes are generally carried out at temperatures above the melting point of the ethylene homopolymer or copolymer product being made. In a typical solution polymerization process, catalyst components, solvent, monomers and hydrogen are fed under pressure to one or more reactors.

For solution phase ethylene polymerization, or ethylene copolymerization, reactor temperatures can range from about 80° C. to about 300° C. while pressures generally range from about 3 MPag to about 45 MPag. The ethylene homopolymer or copolymer produced remains dissolved in the solvent under reactor conditions. The residence time of the solvent in the reactor is relatively short, for example, from about 1 second to about 20 minutes. The solution process can be operated under a wide range of process conditions that allow the production of a wide variety of ethylene polymers. Post reactor, the polymerization reaction is quenched to prevent further polymerization, by adding a catalyst deactivator, and optionally passivated, by adding an acid scavenger. Once deactivated (and optionally passivated), the polymer solution is passed to a polymer recovery operation (a devolatilization system) where the ethylene homopolymer or copolymer is separated from process solvent, unreacted residual ethylene and unreacted optional α-olefin(s).

Regardless of the manner of production, there remains a need to improve the performance of multicomponent polyethylene compositions in film applications.

The present disclosure provides polyethylene compositions which when made into film have a good balance of stiffness, oxygen transmission rates, and sealing properties.

An embodiment of the disclosure is a polyethylene composition including:

from 5 to 80 wt. % of a first polyethylene which is an ethylene copolymer, the first polyethylene having a weight average molecular weight M_(W) of from 70,000 to 250,000, a molecular weight distribution M_(w)/M_(n) of <2.3 and from 5 to 100 short chain branches per thousand carbon atoms;

from 5 to 80 wt. % of a second polyethylene which is an ethylene copolymer or an ethylene homopolymer, the second polyethylene having a weight average molecular weight M_(W) of from 15,000 to 100,000, a molecular weight distribution M_(w)/M_(n) of <2.3 and from 0 to 20 short chain branches per thousand carbon atoms; and

from 5 to 80 wt. % of a third polyethylene which is an ethylene copolymer or an ethylene homopolymer, the third polyethylene having a weight average molecular weight M_(W) of from 70,000 to 250,000, a molecular weight distribution M_(w)/M_(n) of >2.3 and from 0 to 50 short chain branches per thousand carbon atoms; wherein

the number of short chain branches per thousand carbon atoms in the first polyethylene (SCB_(PE-1)) is greater than the number of short chain branches per thousand carbon atoms in the second polyethylene (SCB_(PE-2)) and the third polyethylene (SCB_(PE-3));

the number of short chain branches per thousand carbon atoms in the third polyethylene (SCB_(PE-3)) is greater than the number of short chain branches per thousand carbon atoms in the second polyethylene (SCB_(PE-2)); and

the weight average molecular weight of the second polyethylene is less than the weight average molecular weight of the first polyethylene and the third polyethylene; wherein,

the polyethylene composition has a density of ≤0.939 g/cm³, a melt index I₂ of from 0.1 to 10 dg/min, a melt flow ratio, I₂₁/I₂ of ≤40 and has a soluble fraction in a crystallization elution fractionation (CEF) analysis of at least 10 weight percent.

An embodiment of the disclosure is a film layer having a thickness of from 0.5 to 10 mil, including a polyethylene composition including:

from 5 to 80 wt. % of a first polyethylene which is an ethylene copolymer, the first polyethylene having a weight average molecular weight M_(W) of from 70,000 to 250,000, a molecular weight distribution M_(w)/M_(n) of <2.3 and from 5 to 100 short chain branches per thousand carbon atoms;

from 5 to 80 wt. % of a second polyethylene which is an ethylene copolymer or an ethylene homopolymer, the second polyethylene having a weight average molecular weight M_(W) of from 15,000 to 100,000, a molecular weight distribution M_(w)/M_(n) of <2.3 and from 0 to 20 short chain branches per thousand carbon atoms; and

from 5 to 80 wt. % of a third polyethylene which is an ethylene copolymer or an ethylene homopolymer, the third polyethylene having a weight average molecular weight M_(W) of from 70,000 to 250,000, a molecular weight distribution M_(w)/M_(n) of >2.3 and from 0 to 50 short chain branches per thousand carbon atoms; wherein

the number of short chain branches per thousand carbon atoms in the first polyethylene (SCB_(PE-1)) is greater than the number of short chain branches per thousand carbon atoms in the second polyethylene (SCB_(PE-2)) and the third polyethylene (SCB_(PE-3));

the number of short chain branches per thousand carbon atoms in the third polyethylene (SCB_(PE-3)) is greater than the number of short chain branches per thousand carbon atoms in the second polyethylene (SCB_(PE-2)); and

the weight average molecular weight of the second polyethylene is less than the weight average molecular weight of the first polyethylene and the third polyethylene; wherein,

the polyethylene composition has a density of ≤0.939 g/cm³, a melt index I₂ of from 0.1 to 10 dg/min, a melt flow ratio, I₂₁/I₂ of ≤40 and has a soluble fraction in a crystallization elution fractionation (CEF) analysis of at least 10 weight percent.

In an embodiment, a film layer has a machine direction (MD) 1% secant modulus of ≥190 MPa when measured at a film thickness of about 1 mil.

In an embodiment, a film layer has a seal initiation temperature (SIT) of ≤100° C. when measured at a film thickness of about 2 mil.

In an embodiment, a film layer has an area of hot tack window (AHTW) of ≥160 Newtons·° C. when measured at a film thickness of about 2 mil.

In an embodiment, a film layer has an oxygen transmission rate (OTR) of ≥650 cm³ per 100 inch² per day when measured at a film thickness of about 1 mil.

An embodiment of the disclosure, is a film layer having a thickness of from 0.5 to 10 mil, wherein the film layer has a has a machine direction (MD) 1% secant modulus of ≥190 MPa when measured at a film thickness of about 1 mil, an oxygen transmission rate (OTR) of ≥650 cm³ per 100 inch² per day when measured at a film thickness of about 1 mil, a seal initiation temperature (SIT) of ≤100° C. when measured at a film thickness of about 2 mil, and an area of hot tack window (AHTW) of ≥160 Newtons·® C. when measured at a film thickness of about 2 mil.

An embodiment of the disclosure is a film layer having a thickness of from 0.5 to 10 mil, wherein the film layer satisfies at least one of the following relationships:

i) area of hot tack window (AHTW)>−2.0981 (machine direction (MD) 1% secant modulus)+564.28;

wherein the AHTW is measured at a film thickness of about 2 mil, and the machine direction (MD) 1% secant modulus is measured at a film thickness of about 1 mil;

ii) oxygen transmission rate (OTR)>−5.4297 (machine direction (MD) 1% secant modulus)+1767.8;

wherein the OTR is measured at a film thickness of about 1 mil, and the machine direction (MD) 1% secant modulus is measured at a film thickness of about 1 mil; and

iii) seal initiation temperature (SIT)<0.366 (machine direction (MD) 1% secant modulus)+22.509;

wherein the SIT is measured at a film thickness of about 2 mil, and the machine direction (MD) 1% secant modulus is measured at a film thickness of about 1 mil.

An embodiment of the disclosure is a film layer having a thickness of from 0.5 to 10 mil, wherein the film layer satisfies each of the following relationships:

i) area of hot tack window (AHTW)>−2.0981 (machine direction (MD) 1% secant modulus)+564.28;

wherein the AHTW is measured at a film thickness of about 2 mil, and the machine direction (MD) 1% secant modulus is measured at a film thickness of about 1 mil;

ii) oxygen transmission rate (OTR)>−5.4297 (machine direction (MD) 1% secant modulus)+1767.8;

wherein the OTR is measured at a film thickness of about 1 mil, and the machine direction (MD) 1% secant modulus is measured at a film thickness of about 1 mil; and

iii) seal initiation temperature (SIT)<0.366 (machine direction (MD) 1% secant modulus)+22.509;

wherein the SIT is measured at a film thickness of about 2 mil, and the machine direction (MD) 1% secant modulus is measured at a film thickness of about 1 mil.

BRIEF DESCRIPTION OF THE FIGURES

FIG. 1 shows the gel permeation chromatographs (GPC) with refractive index detection of polyethylene compositions made according to the present disclosure as well as for some comparative polyethylenes.

FIG. 2 shows the gel permeation chromatographs with Fourier transform infra-red (GPC-FTIR) detection obtained for polyethylene compositions made according to the present disclosure as well as for some comparative polyethylenes. The comonomer content, shown as the number of short chain branches per 1000 carbons (y-axis), is given relative to the copolymer molecular weight (x-axis). The upwardly sloping line (from left to right) is the short chain branching (in short chain branches per 1000 carbons atoms) determined by FTIR. As can be seen in the Figure, for Inventive Examples 1 and 2, the number of short chain branches initially increases at higher molecular weights and then decreases again at still higher molecular weights, and hence the comonomer incorporation is said to be “partially reversed” with a peak or maximum present.

FIG. 3 shows the differential scanning calorimetry analysis (DSC) and profile of polyethylene compositions made according to the present disclosure as well as for some comparative polyethylenes.

FIG. 4 shows the hot tack profiles for films made using the polyethylene compositions made according to the present disclosure as well as those for several comparative polyethylenes.

FIG. 5 shows the cold seal profiles for films made using the polyethylene compositions made according to the present disclosure as well as those for several comparative polyethylenes.

FIG. 6 shows a plot of the equation: AHTW=−2.0981 (machine direction (MD) 1% secant modulus)+564.28. The values for the AHTW (the y-axis) are plotted against the corresponding machine direction (MD) 1% secant modulus values (the x-axis) for films made from the polyethylene compositions of the present disclosure as well as those for films made from several comparative polyethylenes.

FIG. 7 shows a plot of the equation: SIT=0.366 (machine direction (MD) 1% secant modulus)+22.509. The values for the SIT (the y-axis) are plotted against the corresponding machine direction (MD) 1% secant modulus values (the x-axis) for films made from the polyethylene compositions of the present disclosure as well as those for films made from several comparative polyethylenes.

FIG. 8 shows a plot of the equation: OTR=−5.4297 (machine direction (MD) 1% secant modulus)+1767.8. The values for the OTR (the y-axis) are plotted against the corresponding machine direction (MD) 1% secant modulus values (the x-axis) for films made from the polyethylene compositions of the present disclosure as well as those for films made from several comparative polyethylenes. “1/2.5 film” means that the film was made at 1 mil of thickness with a blow up ratio (BUR) of 2.5.

DEFINITION OF TERMS

Other than in the examples or where otherwise indicated, all numbers or expressions referring to quantities of ingredients, extrusion conditions, etc., used in the specification and claims are to be understood as modified in all instances by the term “about.” Accordingly, unless indicated to the contrary, the numerical parameters set forth in the following specification and attached claims are approximations that can vary depending upon the desired properties that the various embodiments desire to obtain. At the very least, and not as an attempt to limit the application of the doctrine of equivalents to the scope of the claims, each numerical parameter should at least be construed in light of the number of reported significant digits and by applying ordinary rounding techniques. The numerical values set forth in the specific examples are reported as precisely as possible. Any numerical values, however, inherently contain certain errors necessarily resulting from the standard deviation found in their respective testing measurements.

It should be understood that any numerical range recited herein is intended to include all sub-ranges subsumed therein. For example, a range of “1 to 10” is intended to include all sub-ranges between and including the recited minimum value of 1 and the recited maximum value of 10; that is, having a minimum value equal to or greater than 1 and a maximum value of equal to or less than 10. Because the disclosed numerical ranges are continuous, they include every value between the minimum and maximum values. Unless expressly indicated otherwise, the various numerical ranges specified in this application are approximations.

All compositional ranges expressed herein are limited in total to and do not exceed 100 percent (volume percent or weight percent) in practice. Where multiple components can be present in a composition, the sum of the maximum amounts of each component can exceed 100 percent, with the understanding that, and as those skilled in the art readily understand, that the amounts of the components actually used will conform to the maximum of 100 percent.

In order to form a more complete understanding of this disclosure the following terms are defined and should be used with the accompanying figures and the description of the various embodiments throughout.

As used herein, the term “monomer” refers to a small molecule that may chemically react and become chemically bonded with itself or other monomers to form a polymer.

As used herein, the term “α-olefin” or “alpha-olefin” is used to describe a monomer having a linear hydrocarbon chain containing from 3 to 20 carbon atoms having a double bond at one end of the chain; an equivalent term is “linear α-olefin”.

As used herein, the term “polyethylene” or “ethylene polymer”, refers to macromolecules produced from ethylene monomers and optionally one or more additional monomers; regardless of the specific catalyst or specific process used to make the ethylene polymer. In the polyethylene art, the one or more additional monomers are called “comonomer(s)” and often include α-olefins. The term “homopolymer” refers to a polymer that contains only one type of monomer. An “ethylene homopolymer” is made using only ethylene as a polymerizable monomer. The term “copolymer” refers to a polymer that contains two or more types of monomer. An “ethylene copolymer” is made using ethylene and one or more other types of polymerizable monomer. Common polyethylenes include high density polyethylene (HDPE), medium density polyethylene (MDPE), linear low density polyethylene (LLDPE), very low density polyethylene (VLDPE), ultralow density polyethylene (ULDPE), plastomer and elastomers. The term polyethylene also includes polyethylene terpolymers which may include two or more comonomers in addition to ethylene. The term polyethylene also includes combinations of, or blends of, the polyethylenes described above.

The term “heterogeneously branched polyethylene” refers to a subset of polymers in the ethylene polymer group that are produced using a heterogeneous catalyst system; non-limiting examples of which include Ziegler-Natta or chromium catalysts, both of which are well known in the art.

The term “homogeneously branched polyethylene” refers to a subset of polymers in the ethylene polymer group that are produced using single-site catalysts; non-limiting examples of which include metallocene catalysts, phosphinimine catalysts, and constrained geometry catalysts all of which are well known in the art.

Typically, homogeneously branched polyethylene has narrow molecular weight distributions, for example gel permeation chromatography (GPC) M_(w)/M_(n) values of less than 2.8, for example less than 2.3, although exceptions may arise; M_(w) and M_(n) refer to weight and number average molecular weights, respectively. In contrast, the M_(w)/M_(n) of heterogeneously branched ethylene polymers are typically greater than the M_(w)/M_(n) of homogeneous polyethylene. In general, homogeneously branched ethylene polymers also have a narrow comonomer distribution, i.e. each macromolecule within the molecular weight distribution has a similar comonomer content. Frequently, the composition distribution breadth index “CDBI” is used to quantify how the comonomer is distributed within an ethylene polymer, as well as to differentiate ethylene polymers produced with different catalysts or processes. The “CDBI₅₀” is defined as the percent of ethylene polymer whose composition is within 50 weight percent (wt. %) of the median comonomer composition; this definition is consistent with that described in WO 93/03093 assigned to Exxon Chemical Patents Inc. The CDBI₅₀ of an ethylene interpolymer can be calculated from TREF curves (Temperature Rising Elution Fractionation); the TREF method is described in Wild, et al., J. Polym. Sci., Part B, Polym. Phys., Vol. 20 (3), pages 441-455. Typically, the CDBI₅₀ of homogeneously branched ethylene polymers are greater than about 70% or greater than about 75%. In contrast, the CDBI₅₀ of α-olefin containing heterogeneously branched ethylene polymers are generally lower than the CDBI₅₀ of homogeneous ethylene polymers. For example, the CDBI₅₀ of a heterogeneously branched ethylene polymer may be less than about 75%, or less than about 70%.

It is well known to those skilled in the art, that homogeneously branched ethylene polymers are frequently further subdivided into “linear homogeneous ethylene polymers” and “substantially linear homogeneous ethylene polymers”. These two subgroups differ in the amount of long chain branching: for example, linear homogeneous ethylene polymers have less than about 0.01 long chain branches per 1000 carbon atoms; while substantially linear ethylene polymers have greater than about 0.01 to about 3.0 long chain branches per 1000 carbon atoms. A long chain branch is macromolecular in nature, i.e. similar in length to the macromolecule that the long chain branch is attached to. Hereafter, in this disclosure, the term “homogeneously branched polyethylene” or “homogeneously branched ethylene polymer” refers to both linear homogeneous ethylene polymers and substantially linear homogeneous ethylene polymers.

The term “thermoplastic” refers to a polymer that becomes liquid when heated, will flow under pressure and solidify when cooled. Thermoplastic polymers include ethylene polymers as well as other polymers used in the plastic industry; non-limiting examples of other polymers commonly used in film applications include barrier resins (EVOH), tie resins, polyethylene terephthalate (PET), polyamides and the like.

As used herein the term “monolayer film” refers to a film containing a single layer of one or more thermoplastics.

As used herein, the terms “hydrocarbyl”, “hydrocarbyl radical” or “hydrocarbyl group” refers to linear or cyclic, aliphatic, olefinic, acetylenic and aryl (aromatic) radicals including hydrogen and carbon that are deficient by one hydrogen.

As used herein, an “alkyl radical” includes linear, branched and cyclic paraffin radicals that are deficient by one hydrogen radical; non-limiting examples include methyl (—CH₃) and ethyl (—CH₂CH₃) radicals. The term “alkenyl radical” refers to linear, branched and cyclic hydrocarbons containing at least one carbon-carbon double bond that is deficient by one hydrogen radical.

As used herein, the term “aryl” group includes phenyl, naphthyl, pyridyl and other radicals whose molecules have an aromatic ring structure; non-limiting examples include naphthylene, phenanthrene and anthracene. An “arylalkyl” group is an alkyl group having an aryl group pendant there from; non-limiting examples include benzyl, phenethyl and tolylmethyl; an “alkylaryl” is an aryl group having one or more alkyl groups pendant there from; non-limiting examples include tolyl, xylyl, mesityl and cumyl.

As used herein, the phrase “heteroatom” includes any atom other than carbon and hydrogen that can be bound to carbon. A “heteroatom-containing group” is a hydrocarbon radical that contains a heteroatom and may contain one or more of the same or different heteroatoms. In one embodiment, a heteroatom-containing group is a hydrocarbyl group containing from 1 to 3 atoms chosen from boron, aluminum, silicon, germanium, nitrogen, phosphorous, oxygen and sulfur. Non-limiting examples of heteroatom-containing groups include radicals of imines, amines, oxides, phosphines, ethers, ketones, oxoazolines heterocyclics, oxazolines, thioethers, and the like. The term “heterocyclic” refers to ring systems having a carbon backbone that include from 1 to 3 atoms chosen from boron, aluminum, silicon, germanium, nitrogen, phosphorous, oxygen and sulfur.

As used herein the term “unsubstituted” means that hydrogen radicals are bounded to the molecular group that follows the term unsubstituted. The term “substituted” means that the group following this term possesses one or more moieties that have replaced one or more hydrogen radicals in any position within the group; non-limiting examples of moieties include halogen radicals (F, Cl, Br), hydroxyl groups, carbonyl groups, carboxyl groups, amine groups, phosphine groups, alkoxy groups, phenyl groups, naphthyl groups, C₁ to C₃₀ alkyl groups, C₂ to C₃₀ alkenyl groups, and combinations thereof. Non-limiting examples of substituted alkyls and aryls include: acyl radicals, alkylamino radicals, alkoxy radicals, aryloxy radicals, alkylthio radicals, dialkylamino radicals, alkoxycarbonyl radicals, aryloxycarbonyl radicals, carbomoyl radicals, alkyl- and dialkyl-carbamoyl radicals, acyloxy radicals, acylamino radicals, arylamino radicals and combinations thereof.

In the present disclosure, the polyethylene compositions include at least the following types of polymers: a first polyethylene which is an ethylene copolymer and which has a Mw/Mn of less than about 2.3; a second polyethylene which is an ethylene copolymer or an ethylene homopolymer which is different from the first polyethylene and which has a Mw/Mn of less than about 2.3; and a third polyethylene which is an ethylene copolymer or an ethylene homopolymer which has a Mw/Mn of greater than about 2.3. Each of these polyethylene components, and the polyethylene composition of which they are each a part are further described below.

The First Polyethylene

In an embodiment of the disclosure, the first polyethylene is made with a single site catalyst, non-limiting examples of which include phosphinimine catalysts, metallocene catalysts, and constrained geometry catalysts, all of which are well known in the art.

In an embodiment of the disclosure, the first polyethylene is an ethylene copolymer. Suitable alpha-olefins which may be copolymerized with ethylene to make an ethylene copolymer include 1-propene, 1-butene, 1-pentene, 1-hexene and 1-octene.

In an embodiment of the disclosure, the first polyethylene is a homogeneously branched ethylene copolymer.

In an embodiment of the disclosure, the first polyethylene is an ethylene/1-octene copolymer.

In an embodiment of the disclosure, the first polyethylene is made with a phosphinimine catalyst.

In an embodiment of the disclosure, a phosphinimine catalyst is represented by formula: (L ^(A))_(a) M(Pl)_(b)(Q)_(n) wherein (L^(A)) represents is cyclopentadienyl-type ligand; M represents a metal atom chosen from Ti, Zr, and Hf; Pl represents a phosphinimine ligand; Q represents an activatable ligand; a is 0 or 1; b is 1 or 2; (a+b)=2; n is 1 or 2, and; the sum of (a+b+n) equals the valance of the metal M.

As used herein, the term “cyclopentadienyl-type” ligand is meant to include ligands which contain at least one five-carbon ring which is bonded to the metal via eta-5 (or in some cases eta-3) bonding. Thus, the term “cyclopentadienyl-type” includes, for example, unsubstituted cyclopentadienyl, singly or multiply substituted cyclopentadienyl, unsubstituted indenyl, singly or multiply substituted indenyl, unsubstituted fluorenyl and singly or multiply substituted fluorenyl. Hydrogenated versions of indenyl and fluorenyl ligands are also contemplated for use in the current disclosure, so long as the five-carbon ring which bonds to the metal via eta-5 (or in some cases eta-3) bonding remains intact. Substituents for a cyclopentadienyl ligand, an indenyl ligand (or hydrogenated version thereof) and a fluorenyl ligand (or hydrogenated version thereof) may be chosen from a C₁₋₃₀ hydrocarbyl radical (which hydrocarbyl radical may be unsubstituted or further substituted by for example a halide and/or a hydrocarbyl group; for example a suitable substituted C₁₋₃₀ hydrocarbyl radical is a pentafluorobenzyl group such as —CH₂C₆F₅); a halogen atom; a C₁₋₈ alkoxy radical; a C₆₋₁₀ aryl or aryloxy radical (each of which may be further substituted by for example a halide and/or a hydrocarbyl group); an amido radical which is unsubstituted or substituted by up to two C₁₋₈ alkyl radicals; a phosphido radical which is unsubstituted or substituted by up to two C₁₋₈ alkyl radicals; a silyl radical of the formula —Si(R′)₃ wherein each R′ is independently chosen from hydrogen, a C₁₋₈ alkyl or alkoxy radical, C₆₋₁₀ aryl or aryloxy radicals; and a germanyl radical of the formula —Ge(R′)₃ wherein R′ is as defined directly above.

The phosphinimine ligand, PI, is defined by formula: (R ^(p))₃ P=N— wherein the R^(p) groups are independently chosen from: a hydrogen atom; a halogen atom; C₁₋₂₀ hydrocarbyl radicals which are unsubstituted or substituted with one or more halogen atom(s); a C₁₋₈ alkoxy radical; a C₆₋₁₀ aryl radical; a C₆₋₁₀ aryloxy radical; an amido radical; a silyl radical of formula —Si(R^(s))₃, wherein the R^(s) groups are independently chosen from, a hydrogen atom, a C₁₋₈ alkyl or alkoxy radical, a C₆₋₁₀ aryl radical, a C₆₋₁₀ aryloxy radical, or a germanyl radical of formula —Ge(R^(G))₃, wherein the R^(G) groups are defined as R^(s) is defined in this paragraph.

In an embodiment of the disclosure, the metal, M in the phosphinimine catalyst is titanium, Ti.

In an embodiment of the disclosure, the single site catalyst used to make the first polyethylene is cyclopentadienyl tri(tertiarybutyl)phosphinimine titanium dichloride, Cp((t-Bu)₃PN)TiCl₂.

In an embodiment of the disclosure, the first polyethylene is made with a metallocene catalyst.

In an embodiment of the disclosure, the first polyethylene is made with a bridged metallocene catalyst.

In an embodiment of the disclosure, the first polyethylene is made with a bridged metallocene catalyst having the formula I:

In Formula (I): M is a group 4 metal chosen from titanium, zirconium or hafnium; G is a group 14 element chosen from carbon, silicon, germanium, tin and lead; R₁ is a hydrogen atom, a C₁₋₂₀ hydrocarbyl radical, a C₁₋₂₀ alkoxy radical or a C₆₋₁₀ aryl oxide radical; R₂ and R₃ are independently chosen from a hydrogen atom, a C₁₋₂₀ hydrocarbyl radical, a C₁₋₂₀ alkoxy radical or a C₆₋₁₀ aryl oxide radical; R₄ and R₅ are independently chosen from a hydrogen atom, a C₁₋₂₀ hydrocarbyl radical, a C₁₋₂₀ alkoxy radical or a C₆₋₁₀ aryl oxide radical; and Q is independently an activatable leaving group ligand.

In the current disclosure, the term “activatable”, means that the ligand Q may be cleaved from the metal center M via a protonolysis reaction or abstracted from the metal center M by suitable acidic or electrophilic catalyst activator compounds (also known as “co-catalyst” compounds) respectively, examples of which are described below. The activatable ligand Q may also be transformed into another ligand which is cleaved or abstracted from the metal center M (e.g. a halide may be converted to an alkyl group). Without wishing to be bound by any single theory, protonolysis or abstraction reactions generate an active “cationic” metal center which can polymerize olefins.

In embodiments of the present disclosure, the activatable ligand, Q is independently chosen from a hydrogen atom; a halogen atom; a C₁₋₂₀ hydrocarbyl radical, a C₁₋₂₀ alkoxy radical, and a C₆₋₁₀ aryl or aryloxy radical, where each of the hydrocarbyl, alkoxy, aryl, or aryl oxide radicals may be un-substituted or further substituted by one or more halogen or other group; a C₁₋₈ alkyl; a C₁₋₈ alkoxy; a C₆₋₁₀ aryl or aryloxy; an amido or a phosphido radical, but where Q is not a cyclopentadienyl. Two Q ligands may also be joined to one another and form for example, a substituted or unsubstituted diene ligand (e.g. 1,3-butadiene); or a delocalized heteroatom containing group such as an acetate or acetamidinate group. In a convenient embodiment of the disclosure, each Q is independently chosen from a halide atom, a C₁₋₄ alkyl radical and a benzyl radical. Particularly suitable activatable ligands Q are monoanionic such as a halide (e.g. chloride) or a hydrocarbyl (e.g. methyl, benzyl).

In an embodiment of the disclosure, the single site catalyst used to make the first polyethylene is diphenylmethylene(cyclopentadienyl)(2,7-di-t-butylfuorenyl)hafnium dichloride having the molecular formula: [(2,7-tBu₂Flu)Ph₂C(Cp)HfCl₂].

In an embodiment of the disclosure the single site catalyst used to make the first polyethylene has is diphenylmethylene(cyclopentadienyl)(2,7-di-t-butylfuorenyl)hafnium dimethyl having the molecular formula [(2,7-tBu₂Flu)Ph₂C(Cp)HfMe₂].

In addition to the single site catalyst molecule per se, an active single site catalyst system may further include one or more of the following: an alkylaluminoxane co-catalyst and an ionic activator. The single site catalyst system may also optionally include a hindered phenol.

Although the exact structure of alkylaluminoxane is uncertain, subject matter experts generally agree that it is an oligomeric species that contain repeating units of the general formula: (R)₂ AlO—(Al(R)—O)_(n) —Al(R)₂ where the R groups may be the same or different linear, branched or cyclic hydrocarbyl radicals containing 1 to 20 carbon atoms and n is from 0 to about 50. A non-limiting example of an alkylaluminoxane is methylaluminoxane (or MAO) wherein each R group is a methyl radical.

In an embodiment of the disclosure, R of the alkylaluminoxane, is a methyl radical and m is from 10 to 40.

In an embodiment of the disclosure, the co-catalyst is modified methylaluminoxane (MMAO).

It is well known in the art, that the alkylaluminoxane can serve dual roles as both an alkylator and an activator. Hence, an alkylaluminoxane co-catalyst is often used in combination with activatable ligands such as halogens.

In general, ionic activators are comprised of a cation and a bulky anion; wherein the latter is substantially non-coordinating. Non-limiting examples of ionic activators are boron ionic activators that are four coordinate with four ligands bonded to the boron atom. Non-limiting examples of boron ionic activators include the following formulas shown below; [R ₅]⁺[B(R ⁷)₄]⁻ where B represents a boron atom, R⁵ is an aromatic hydrocarbyl (e.g. triphenyl methyl cation) and each R⁷ is independently chosen from phenyl radicals which are unsubstituted or substituted with from 3 to 5 substituents chosen from fluorine atoms, C₁₋₄ alkyl or alkoxy radicals which are unsubstituted or substituted by fluorine atoms; and a silyl radical of formula —Si(R⁹)₃, where each R⁹ is independently chosen from hydrogen atoms and C₁₋₄ alkyl radicals, and [(R ⁸)_(t) ZH]⁺[B(R ⁷)₄]⁻ where B is a boron atom, H is a hydrogen atom, Z is a nitrogen or phosphorus atom, t is 2 or 3 and R⁸ is chosen from C₁₋₈ alkyl radicals, and phenyl radicals which are unsubstituted or substituted by up to three C₁₋₄ alkyl radicals, or wherein one R⁸ taken together with the nitrogen atom may form an anilinium radical and R⁷ is as defined above.

In both formula a non-limiting example of R⁷ is a pentafluorophenyl radical. In general, boron ionic activators may be described as salts of tetra(perfluorophenyl) boron; non-limiting examples include anilinium, carbonium, oxonium, phosphonium and sulfonium salts of tetra(perfluorophenyl)boron with anilinium and trityl (or triphenylmethylium). Additional non-limiting examples of ionic activators include: triethylammonium tetra(phenyl)boron, tripropylammonium tetra(phenyl)boron, tri(n-butyl)ammonium tetra(phenyl)boron, trimethylammonium tetra(p-tolyl)boron, trimethylammonium tetra(o-tolyl)boron, tributylammonium tetra(pentafluorophenyl)boron, tripropylammonium tetra(o,p-dimethylphenyl)boron, tributylammonium tetra(m,m-dimethylphenyl)boron, tributylammonium tetra(p-trifluoromethylphenyl)boron, tributylammonium tetra(pentafluorophenyl)boron, tri(n-butyl)ammonium tetra(o-tolyl)boron, N,N-dimethylanilinium tetra(phenyl)boron, N,N-diethylanilinium tetra(phenyl)boron, N,N-diethylanilinium tetra(phenyl)n-butylboron, N,N-2,4,6-pentamethylanilinium tetra(phenyl)boron, di-(isopropyl)ammonium tetra(pentafluorophenyl) boron, dicyclohexylammonium tetra(phenyl)boron, triphenylphosphonium tetra(phenyl)boron, tri(methylphenyl)phosphonium tetra(phenyl)boron, tri(dimethylphenyl)phosphonium tetra(phenyl)boron, tropillium tetrakispentafluorophenyl borate, triphenylmethylium tetrakispentafluorophenyl borate, benzene(diazonium)tetrakispentafluorophenyl borate, tropillium tetrakis(2,3,5,6-tetrafluorophenyl)borate, triphenylmethylium tetrakis(2,3,5,6-tetrafluorophenyl)borate, benzene(diazonium) tetrakis(3,4,5-trifluorophenyl)borate, tropillium tetrakis(3,4,5-trifluorophenyl)borate, benzene(diazonium) tetrakis(3,4,5-trifluorophenyl)borate, tropillium tetrakis(1,2,2-trifluoroethenyl)borate, triphenylmethylium tetrakis(1,2,2-trifluoroethenyl)borate, benzene(diazonium) tetrakis(1,2,2-trifluoroethenyl)borate, tropillium tetrakis(2,3,4,5-tetrafluorophenyl)borate, triphenylmethylium tetrakis(2,3,4,5-tetrafluorophenyl)borate, and benzene(diazonium) tetrakis(2,3,4,5 tetrafluorophenyl)borate. Readily available commercial ionic activators include N,N-dimethylanilinium tetrakispentafluorophenyl borate, and triphenylmethylium tetrakispentafluorophenyl borate.

Non-limiting example of hindered phenols include butylated phenolic antioxidants, butylated hydroxytoluene, 2,6-di-tertiarybutyl-4-ethyl phenol, 4,4′-methylenebis (2,6-di-tertiary-butylphenol), 1,3,5-trimethyl-2,4,6-tris (3,5-di-tert-butyl-4-hydroxybenzyl) benzene and octadecyl-3-(3′,5′-di-tert-butyl-4′-hydroxyphenyl) propionate.

To produce an active single site catalyst system the quantity and mole ratios of the three or four components: the single site catalyst, the alkylaluminoxane, the ionic activator, and the optional hindered phenol are optimized.

In an embodiment of the disclosure, the single site catalyst used to make the first polyethylene produces no long chain branches, and the first polyethylene will contain no measurable amounts of long chain branches.

In an embodiment of the disclosure, the single site catalyst used to make the first polyethylene produces long chain branches, and the first polyethylene will contain long chain branches, hereinafter “LCB”. LCB is a well-known structural phenomenon in polyethylenes and well known to those of ordinary skill in the art. Traditionally, there are three methods for LCB analysis, namely, nuclear magnetic resonance spectroscopy (NMR), for example see J. C. Randall, J Macromol. Sci., Rev. Macromol. Chem. Phys. 1989, 29, 201; triple detection SEC equipped with a DRI, a viscometer and a low-angle laser light scattering detector, for example see W. W. Yau and D. R. Hill, Int. J. Polym. Anal. Charact. 1996; 2:151; and rheology, for example see W. W. Graessley, Acc. Chem. Res. 1977, 10, 332-339. In this disclosure, a long chain branch is macromolecular in nature, i.e. long enough to be seen in an NMR spectra, triple detector SEC experiments or rheological experiments.

In embodiments of the disclosure, the upper limit on the molecular weight distribution, M_(w)/M_(n) of the first polyethylene may be about 2.8, or about 2.5, or about 2.4, or about 2.3, or about 2.2. In embodiments of the disclosure, the lower limit on the molecular weight distribution, M_(w)/M_(n) of the first polyethylene may be about 1.4, or about 1.6, or about 1.7, or about 1.8, or about 1.9.

In embodiments of the disclosure, the first polyethylene has a molecular weight distribution, M_(w)/M_(n) of <2.3, or <2.1, or <2.0 or about 2.0. In embodiments of the disclosure, the first polyethylene has a molecular weight distribution, M_(w)/M_(n) of from about 1.7 to about 2.2.

In an embodiment of the disclosure, the first polyethylene has from 1 to 200 short chain branches per thousand carbon atoms (SCB_(PE-1)). In further embodiments, the first polyethylene has from 3 to 150 short chain branches per thousand carbon atoms (SCB_(PE-1)), or from 5 to 100 short chain branches per thousand carbon atoms (SCB_(PE-1)), or from 10 to 100 short chain branches per thousand carbon atoms (SCB_(PE-1)), or from 5 to 75 short chain branches per thousand carbon atoms (SCB_(PE-1)), or from 10 to 75 short chain branches per thousand carbon atoms (SCB_(PE-1)), or from 15 to 75 short chain branches per thousand carbon atoms (SCB_(PE-1)), or from 20 to 75 short chain branches per thousand carbon atoms (SCB_(PE-1)). In still further embodiments, the first polyethylene has from 20 to 100 short chain branches per thousand carbon atoms (SCB_(PE-1)), or from 25 to 100 short chain branches per thousand carbon atoms (SCB_(PE-1)), or from 30 to 100 short chain branches per thousand carbon atoms (SCB_(PE-1)), or from 35 to 100 short chain branches per thousand carbon atoms (SCB_(PE-1)), or from 35 to 75 short chain branches per thousand carbon atoms (SCB_(PE-1)), or from 30 to 75 short chain branches per thousand carbon atoms (SCB_(PE-1)), or from 30 to 60 short chain branches per thousand carbon atoms (SCB_(PE-1)), or from 30 to 50 short chain branches per thousand carbon atoms (SCB_(PE-1)), or from 35 to 60 short chain branches per thousand carbon atoms (SCB_(PE-1)), or from 35 to 55 short chain branches per thousand carbon atoms (SCB_(PE-1)).

The short chain branching (i.e. the short chain branching per thousand carbons, SCB_(PE-1)) is the branching due to the presence of an alpha-olefin comonomer in the polyethylene and will for example have two carbon atoms for a 1-butene comonomer, or four carbon atoms for a 1-hexene comonomer, or six carbon atoms for a 1-octene comonomer, etc.

In an embodiment of the disclosure, the number of short chain branches per thousand carbon atoms in the first polyethylene (SCB_(PE-1)), is greater than the number of short chain branches per thousand carbon atoms in the second polyethylene (SCB_(PE-2)).

In an embodiment of the disclosure, the number of short chain branches per thousand carbon atoms in the first polyethylene (SCB_(PE-1)), is greater than the number of short chain branches per thousand carbon atoms in the third polyethylene (SCB_(PE-3)).

In an embodiment of the disclosure, the number of short chain branches per thousand carbon atoms in the first polyethylene (SCB_(PE-1)), is greater than the number of short chain branches per thousand carbon atoms in each of the second polyethylene (SCB_(PE-2)) and the third polyethylene (SCB_(PE-3)).

In embodiments of the disclosure, the upper limit on the density, d1 of the first polyethylene may be about 0.975 g/cm³; in some cases about 0.965 g/cm³ and; in other cases about 0.955 g/cm³. In embodiments of the disclosure, the lower limit on the density, d1 of the first polyethylene may be about 0.855 g/cm³, in some cases about 0.865 g/cm³, and; in other cases about 0.875 g/cm³.

In embodiments of the disclosure the density, d1 of the first polyethylene may be from about 0.855 to about 0.965 g/cm³, or from 0.865 g/cm³ to about 0.965 g/cm³, or from about 0.870 g/cm³ to about 0.960 g/cm³, or from about 0.865 g/cm³ to 0.950 g/cm³, or from about 0.865 g/cm³ to about 0.940 g/cm³, or from about 0.865 g/cm³ to about 0.936 g/cm³, or from about 0.860 g/cm³ to about 0.932 g/cm³, or from about 0.865 g/cm³ to about 0.926 g/cm³, or from about 0.865 g/cm³ to about 0.921 g/cm³, or from about 0.865 g/cm³ to about 0.918 g/cm³, or from about 0.865 g/cm³ to about 0.916 g/cm³, or from about 0.870 g/cm³ to about 0.916 g/cm³, or from about 0.865 g/cm³ to about 0.912 g/cm³, or from about 0.865 g/cm³ to about 0.910 g/cm³, or from about 0.865 g/cm³ to about 0.905 g/cm³, or from about 0.865 g/cm³ to about 0.900 g/cm³, or from about 0.855 g/cm³ to about 0.900 g/cm³, or from about 0.855 g/cm³ to about 0.905 g/cm³, or from about 0.855 g/cm³ to about 0.910 g/cm³, or from about 0.855 g/cm³ to about 0.916 g/cm³.

In embodiments of the disclosure, the upper limit on the CDBI₅₀ of the first polyethylene may be about 98 weight %, in other cases about 95 wt % and in still other cases about 90 wt. %. In embodiments of the disclosure, the lower limit on the CDBI₅₀ of the first polyethylene may be about 70 weight %, in other cases about 75 wt. % and in still other cases about 80 wt. %.

In embodiments of the disclosure the melt index of the first polyethylene I₂ ¹ may be from about 0.01 dg/min to about 1000 dg/min, or from about 0.01 dg/min to about 500 dg/min, or from about 0.01 dg/min to about 100 dg/min, or from about 0.01 dg/min to about 50 dg/min, or from about 0.01 dg/min to about 25 dg/min, or from about 0.01 dg/min to about 10 dg/min, or from about 0.01 dg/min to about 5 dg/min, or from about 0.01 dg/min to about 3 dg/min, or from about 0.01 dg/min to about 1 dg/min, or less than about 5 dg/min, or less than about 3 dg/min, or less than about 1.0 dg/min, or less than about 0.75 dg/min, or less than about 0.50 dg/min.

In an embodiment of the disclosure, the first polyethylene has a weight average molecular weight, M_(w) of from about 50,000 to about 300,000, or from about 50,000 to about 250,000, or from about 60,000 to about 250,000, or from about 70,000 to about 250,000 or from about 60,000 to about 220,000, or from about 70,000 to about 200,000, or from about 75,000 to about 200,000, or from about 75,000 to about 175,000; or from about 70,000 to about 175,000, or from about 70,000 to about 150,000.

In an embodiment of the disclosure, the first polyethylene has a weight average molecular weight, M_(w) which is greater than the weight average molecular weight, M_(w) of the second polyethylene.

In an embodiment of the disclosure, the first polyethylene has a weight average molecular weight, M_(w) which is greater than the weight average molecular weight, M_(w) of the third polyethylene.

In an embodiment of the disclosure, the first polyethylene has a weight average molecular weight, M_(w) which is within 30 percent of the weight average molecular weight, M_(w) of the third polyethylene. For clarity, this means that: the absolute difference between the weight average molecular weight, M_(w) of the first polyethylene and the weight average molecular weight, M_(w) of the third polyethylene divided by the weight average molecular weight, M_(w) of the third polyethylene and converted to a percentage (i.e. [|Mw1−Mw3|/Mw3]×100%) is within 25 percent.

In an embodiment of the disclosure, the first polyethylene has a weight average molecular weight, M_(w) which is within 25 percent of the weight average molecular weight, M_(w) of the third polyethylene. In an embodiment of the disclosure, the first polyethylene has a weight average molecular weight, M_(w) which is within 20 percent of the weight average molecular weight, M_(w) of the third polyethylene. In an embodiment of the disclosure, the first polyethylene has a weight average molecular weight, M_(w) which is within 15 percent of the weight average molecular weight, M_(w) of the third polyethylene. In an embodiment of the disclosure, the first polyethylene has a weight average molecular weight, M_(w) which is within 10 percent of the weight average molecular weight, M_(w) of the third polyethylene.

In embodiments of the disclosure, the upper limit on the weight percent (wt. %) of the first polyethylene in the polyethylene composition (i.e. the weight percent of the first polyethylene based on the total weight of the first, the second and the third polyethylene) may be about 80 wt. %, or about 75 wt. %, or about 70 wt. %, or about 65 wt. %, or about 60 wt. %, or about 55 wt. % or about 50 wt. %, or about 45%, or about 40%, or about 35%. In embodiments of the disclosure, the lower limit on the wt. % of the first polyethylene in the polyethylene composition may be about 1 wt. %, or about 5 wt. %, or about 10 wt. %, or about 15 wt. %, or about 20 wt. %, or about 25 wt. % or in other cases about 30 wt. %.

The Second Polyethylene

In an embodiment of the disclosure, the second polyethylene is made with a single site catalyst, non-limiting examples of which include phosphinimine catalysts, metallocene catalysts, and constrained geometry catalysts, all of which are well known in the art.

In an embodiment of the disclosure, the second polyethylene is an ethylene homopolymer.

In an embodiment of the disclosure, the second polyethylene is an ethylene copolymer. Suitable alpha-olefins which may be copolymerized with ethylene to make an ethylene copolymer include 1-propene, 1-butene, 1-pentene, 1-hexene and 1-octene.

In an embodiment of the disclosure, the second polyethylene is a homogeneously branched ethylene copolymer.

In an embodiment of the disclosure, the second polyethylene is an ethylene/1-octene copolymer.

In an embodiment of the disclosure, the second polyethylene is made with a phosphinimine catalyst.

In an embodiment of the disclosure, a phosphinimine catalyst is represented by formula: (L ^(A))_(a) M(Pl)_(b)(Q)_(n) wherein (L^(A)) represents is cyclopentadienyl-type ligand; M represents a metal atom chosen from Ti, Zr, and Hf; Pl represents a phosphinimine ligand; Q represents an activatable ligand; a is 0 or 1; b is 1 or 2; (a+b)=2; n is 1 or 2, and; the sum of (a+b+n) equals the valance of the metal M.

As used herein, the term “cyclopentadienyl-type” ligand is meant to include ligands which contain at least one five-carbon ring which is bonded to the metal via eta-5 (or in some cases eta-3) bonding. Thus, the term “cyclopentadienyl-type” includes, for example, unsubstituted cyclopentadienyl, singly or multiply substituted cyclopentadienyl, unsubstituted indenyl, singly or multiply substituted indenyl, unsubstituted fluorenyl and singly or multiply substituted fluorenyl. Hydrogenated versions of indenyl and fluorenyl ligands are also contemplated for use in the current disclosure, so long as the five-carbon ring which bonds to the metal via eta-5 (or in some cases eta-3) bonding remains intact. Substituents for a cyclopentadienyl ligand, an indenyl ligand (or hydrogenated version thereof) and a fluorenyl ligand (or hydrogenated version thereof) may be chosen from a C₁₋₃₀ hydrocarbyl radical (which hydrocarbyl radical may be unsubstituted or further substituted by for example a halide and/or a hydrocarbyl group; for example a suitable substituted C₁-30 hydrocarbyl radical is a pentafluorobenzyl group such as —CH₂C₆F₅); a halogen atom; a C₁₋₈ alkoxy radical; a C₆₋₁₀ aryl or aryloxy radical (each of which may be further substituted by for example a halide and/or a hydrocarbyl group); an amido radical which is unsubstituted or substituted by up to two C₁₋₈ alkyl radicals; a phosphido radical which is unsubstituted or substituted by up to two C₁₋₈ alkyl radicals; a silyl radical of the formula —Si(R′)₃ wherein each R′ is independently chosen from hydrogen, a C₁₋₈ alkyl or alkoxy radical, C₆₋₁₀ aryl or aryloxy radicals; and a germanyl radical of the formula —Ge(R′)₃ wherein R′ is as defined directly above.

The phosphinimine ligand, PI, is defined by formula: (R ^(p))₃ P=N— wherein the R^(p) groups are independently chosen from: a hydrogen atom; a halogen atom; C₁₋₂₀ hydrocarbyl radicals which are unsubstituted or substituted with one or more halogen atom(s); a C₁₋₈ alkoxy radical; a C₆₋₁₀ aryl radical; a C₆₋₁₀ aryloxy radical; an amido radical; a silyl radical of formula —Si(R^(s))₃, wherein the R^(s) groups are independently chosen from, a hydrogen atom, a C₁₋₈ alkyl or alkoxy radical, a C₆₋₁₀ aryl radical, a C₆₋₁₀ aryloxy radical, or a germanyl radical of formula —Ge(R^(G))₃, wherein the R^(G) groups are defined as R^(s) is defined in this paragraph.

In an embodiment of the disclosure, the metal, M in the phosphinimine catalyst is titanium, Ti.

In an embodiment of the disclosure, the single site catalyst used to make the second polyethylene is cyclopentadienyl tri(tertiarybutyl)phosphinimine titanium dichloride, Cp((t-Bu)₃PN)TiCl₂.

In an embodiment of the disclosure, the second polyethylene is made with a metallocene catalyst.

In an embodiment of the disclosure, the second polyethylene is made with a bridged metallocene catalyst.

In an embodiment of the disclosure, the second polyethylene is made with a bridged metallocene catalyst having the formula I:

In Formula (I): M is a group 4 metal chosen from titanium, zirconium or hafnium; G is a group 14 element chosen from carbon, silicon, germanium, tin or lead; R₁ is a hydrogen atom, a C₁₋₂₀ hydrocarbyl radical, a C₁₋₂₀ alkoxy radical or a C₆₋₁₀ aryl oxide radical; R₂ and R₃ are independently chosen from a hydrogen atom, a C₁₋₂₀ hydrocarbyl radical, a C₁₋₂₀ alkoxy radical or a C₆₋₁₀ aryl oxide radical; R₄ and R₅ are independently chosen from a hydrogen atom, a C₁₋₂₀ hydrocarbyl radical, a C₁₋₂₀ alkoxy radical or a C₆₋₁₀ aryl oxide radical; and Q is independently an activatable leaving group ligand.

In the current disclosure, the term “activatable”, means that the ligand Q may be cleaved from the metal center M via a protonolysis reaction or abstracted from the metal center M by suitable acidic or electrophilic catalyst activator compounds (also known as “co-catalyst” compounds) respectively, examples of which are described below. The activatable ligand Q may also be transformed into another ligand which is cleaved or abstracted from the metal center M (e.g. a halide may be converted to an alkyl group). Without wishing to be bound by any single theory, protonolysis or abstraction reactions generate an active “cationic” metal center which can polymerize olefins.

In embodiments of the present disclosure, the activatable ligand, Q is independently chosen from a hydrogen atom; a halogen atom; a C₁₋₂₀ hydrocarbyl radical, a C₁₋₂₀ alkoxy radical, and a C₆₋₁₀ aryl or aryloxy radical, where each of the hydrocarbyl, alkoxy, aryl, or aryl oxide radicals may be un-substituted or further substituted by one or more halogen or other group; a C₁₋₈ alkyl; a C₁₋₈ alkoxy; a C₆₋₁₀ aryl or aryloxy; an amido or a phosphido radical, but where Q is not a cyclopentadienyl. Two Q ligands may also be joined to one another and form for example, a substituted or unsubstituted diene ligand (e.g. 1,3-butadiene); or a delocalized heteroatom containing group such as an acetate or acetamidinate group. In a convenient embodiment of the disclosure, each Q is independently chosen from a halide atom, a C₁₋₄ alkyl radical and a benzyl radical. Particularly suitable activatable ligands Q are monoanionic such as a halide (e.g. chloride) or a hydrocarbyl (e.g. methyl, benzyl).

In an embodiment of the disclosure, the single site catalyst used to make the second polyethylene is diphenylmethylene(cyclopentadienyl)(2,7-di-t-butylfuorenyl)hafnium dichloride having the molecular formula: [(2,7-tBu₂Flu)Ph₂C(Cp)HfCl₂].

In an embodiment of the disclosure the single site catalyst used to make the second polyethylene has is diphenylmethylene(cyclopentadienyl)(2,7-di-t-butylfuorenyl)hafnium dimethyl having the molecular formula [(2,7-tBu₂Flu)Ph₂C(Cp)HfMe₂].

In addition to the single site catalyst molecule per se, an active single site catalyst system may further include one or more of the following: an alkylaluminoxane co-catalyst and an ionic activator. The single site catalyst system may also optionally include a hindered phenol.

Although the exact structure of alkylaluminoxane is uncertain, subject matter experts generally agree that it is an oligomeric species that contain repeating units of the general formula: (R)₂ AlO—(Al(R)—O)_(n) —Al(R)₂ where the R groups may be the same or different linear, branched or cyclic hydrocarbyl radicals containing 1 to 20 carbon atoms and n is from 0 to about 50. A non-limiting example of an alkylaluminoxane is methylaluminoxane (or MAO) wherein each R group is a methyl radical.

In an embodiment of the disclosure, R of the alkylaluminoxane, is a methyl radical and m is from 10 to 40.

In an embodiment of the disclosure, the co-catalyst is modified methylaluminoxane (MMAO).

It is well known in the art, that the alkylaluminoxane can serve dual roles as both an alkylator and an activator. Hence, an alkylaluminoxane co-catalyst is often used in combination with activatable ligands such as halogens.

In general, ionic activators are comprised of a cation and a bulky anion; wherein the latter is substantially non-coordinating. Non-limiting examples of ionic activators are boron ionic activators that are four coordinate with four ligands bonded to the boron atom. Non-limiting examples of boron ionic activators include the following formulas shown below; [R ⁵]⁺[B(R ⁷)₄]⁻ where B represents a boron atom, R⁵ is an aromatic hydrocarbyl (e.g. triphenyl methyl cation) and each R⁷ is independently chosen from phenyl radicals which are unsubstituted or substituted with from 3 to 5 substituents chosen from fluorine atoms, C₁₋₄ alkyl or alkoxy radicals which are unsubstituted or substituted by fluorine atoms; and a silyl radical of formula —Si(R⁹)₃, where each R⁹ is independently chosen from hydrogen atoms and C₁₋₄ alkyl radicals, and [(R ⁸)_(t) ZH]⁺[B(R ⁷)₄]⁻ where B is a boron atom, H is a hydrogen atom, Z is a nitrogen or phosphorus atom, t is 2 or 3 and R⁸ is chosen from C₁₋₈ alkyl radicals, phenyl radicals which are unsubstituted or substituted by up to three C₁₋₄ alkyl radicals, or wherein one R⁸ taken together with the nitrogen atom may form an anilinium radical and R⁷ is as defined above.

In both formula a non-limiting example of R⁷ is a pentafluorophenyl radical. In general, boron ionic activators may be described as salts of tetra(perfluorophenyl) boron; non-limiting examples include anilinium, carbonium, oxonium, phosphonium and sulfonium salts of tetra(perfluorophenyl)boron with anilinium and trityl (or triphenylmethylium). Additional non-limiting examples of ionic activators include: triethylammonium tetra(phenyl)boron, tripropylammonium tetra(phenyl)boron, tri(n-butyl)ammonium tetra(phenyl)boron, trimethylammonium tetra(p-tolyl)boron, trimethylammonium tetra(o-tolyl)boron, tributylammonium tetra(pentafluorophenyl)boron, tripropylammonium tetra(o,p-dimethylphenyl)boron, tributylammonium tetra(m,m-dimethylphenyl)boron, tributylammonium tetra(p-trifluoromethylphenyl)boron, tributylammonium tetra(pentafluorophenyl)boron, tri(n-butyl)ammonium tetra(o-tolyl)boron, N,N-dimethylanilinium tetra(phenyl)boron, N,N-diethylanilinium tetra(phenyl)boron, N,N-diethylanilinium tetra(phenyl)n-butylboron, N,N-2,4,6-pentamethylanilinium tetra(phenyl)boron, di-(isopropyl)ammonium tetra(pentafluorophenyl)boron, dicyclohexylammonium tetra(phenyl)boron, triphenylphosphonium tetra(phenyl)boron, tri(methylphenyl)phosphonium tetra(phenyl)boron, tri(dimethylphenyl)phosphonium tetra(phenyl)boron, tropillium tetrakispentafluorophenyl borate, triphenylmethylium tetrakispentafluorophenyl borate, benzene(diazonium)tetrakispentafluorophenyl borate, tropillium tetrakis(2,3,5,6-tetrafluorophenyl)borate, triphenylmethylium tetrakis(2,3,5,6-tetrafluorophenyl)borate, benzene(diazonium) tetrakis(3,4,5-trifluorophenyl)borate, tropillium tetrakis(3,4,5-trifluorophenyl)borate, benzene(diazonium) tetrakis(3,4,5-trifluorophenyl)borate, tropillium tetrakis(1,2,2-trifluoroethenyl)borate, triphenylmethylium tetrakis(1,2,2-trifluoroethenyl)borate, benzene(diazonium) tetrakis(1,2,2-trifluoroethenyl)borate, tropillium tetrakis(2,3,4,5-tetrafluorophenyl)borate, triphenylmethylium tetrakis(2,3,4,5-tetrafluorophenyl)borate, and benzene(diazonium) tetrakis(2,3,4,5 tetrafluorophenyl)borate. Readily available commercial ionic activators include N,N-dimethylanilinium tetrakispentafluorophenyl borate, and triphenylmethylium tetrakispentafluorophenyl borate.

Non-limiting example of hindered phenols include butylated phenolic antioxidants, butylated hydroxytoluene, 2,6-di-tertiarybutyl-4-ethyl phenol, 4,4′-methylenebis (2,6-di-tertiary-butylphenol), 1,3,5-trimethyl-2,4,6-tris (3,5-di-tert-butyl-4-hydroxybenzyl) benzene and octadecyl-3-(3′,5′-di-tert-butyl-4′-hydroxyphenyl) propionate.

To produce an active single site catalyst system the quantity and mole ratios of the three or four components: the single site catalyst, the alkylaluminoxane, the ionic activator, and the optional hindered phenol are optimized.

In an embodiment of the disclosure, the single site catalyst used to make the second polyethylene produces no long chain branches, and the second polyethylene will contain no measurable amounts of long chain branches.

In an embodiment of the disclosure, the single site catalyst used to make the second polyethylene produces long chain branches, and the second polyethylene will contain long chain branches, hereinafter “LCB”. LCB is a well-known structural phenomenon in polyethylenes and well known to those of ordinary skill in the art. Traditionally, there are three methods for LCB analysis, namely, nuclear magnetic resonance spectroscopy (NMR), for example see J. C. Randall, J Macromol. Sci., Rev. Macromol. Chem. Phys. 1989, 29, 201; triple detection SEC equipped with a DRI, a viscometer and a low-angle laser light scattering detector, for example see W. W. Yau and D. R. Hill, Int. J. Polym. Anal. Charact. 1996; 2:151; and rheology, for example see W. W. Graessley, Acc. Chem. Res. 1977, 10, 332-339. In this disclosure, a long chain branch is macromolecular in nature, i.e. long enough to be seen in an NMR spectra, triple detector SEC experiments or rheological experiments.

In embodiments of the disclosure, the upper limit on the molecular weight distribution, M_(w)/M_(n) of the second polyethylene may be about 2.8, or about 2.5, or about 2.4, or about 2.3, or about 2.2. In embodiments of the disclosure, the lower limit on the molecular weight distribution, M_(w)/M_(n) of the second polyethylene may be about 1.4, or about 1.6, or about 1.7, or about 1.8, or about 1.9.

In embodiments of the disclosure, the second polyethylene has a molecular weight distribution, M_(w)/M_(n) of <2.3, or <2.1, or <2.0 or about 2.0. In embodiments of the disclosure, the second polyethylene has a molecular weight distribution, M_(w)/M_(n) of from about 1.7 to about 2.2.

In an embodiment of the disclosure, the second polyethylene has from 0 to 100 short chain branches per thousand carbon atoms (SCB_(PE-2)). In further embodiments, the second polyethylene has from 0 to 30 short chain branches per thousand carbon atoms (SCB_(PE-2)), or from 0 to 20 short chain branches per thousand carbon atoms (SCB_(PE-2)), or from 0 to 15 short chain branches per thousand carbon atoms (SCB_(PE-2)), or from 0 to 10 short chain branches per thousand carbon atoms (SCB_(PE-2)), or from 0 to 5 short chain branches per thousand carbon atoms (SCB_(PE-2)), or fewer than 5 short chain branches per thousand carbon atoms (SCB_(PE-2)), or fewer than 3 short chain branches per thousand carbon atoms (SCB_(PE-2)), or fewer than 1 short chain branches per thousand carbon atoms (SCB_(PE2)), or about zero short chain branches per thousand carbon atoms (SCB_(PE-2)).

The short chain branching (i.e. the short chain branching per thousand carbons, SCB_(PE-1)) is the branching due to the presence of an alpha-olefin comonomer in the polyethylene and will for example have two carbon atoms for a 1-butene comonomer, or four carbon atoms for a 1-hexene comonomer, or six carbon atoms for a 1-octene comonomer, etc.

In embodiments of the disclosure, the upper limit on the density, d2 of the second polyethylene may be about 0.985 g/cm³; in some cases, about 0.975 g/cm³ and; in other cases, about 0.965 g/cm³. In embodiments of the disclosure, the lower limit on the density, d2 of the second polyethylene may be about 0.921 g/cm³, in some cases about 0.932 g/cm³, and; in other cases about 0.949 g/cm³.

In embodiments of the disclosure the density, d2 of the second polyethylene may be from about 0.921 g/cm³ to about 0.980 g/cm³, or from about 0.921 g/cm³ to about 0.975 g/cm³, or from about 0.926 g/cm³ to about 0.975 g/cm³, or from about 0.930 g/cm³ to about 0.975 g/cm³, or from about 0.936 g/cm³ to about 0.975 g/cm³, or from about 0.940 g/cm³ to about 0.975 g/cm³, or from about 0.940 g/cm³ to about 0.980 g/cm³, or from about 0.945 g/cm³ to about 0.975 g/cm³, or from about 0.950 g/cm³ to about 0.975 g/cm³, or from about 0.951 g/cm³ to about 0.975 g/cm³, or from about 0.953 g/cm³ to about 0.975 g/cm³, or from about 0.953 g/cm³ to about 0.985 g/cm³.

In embodiments of the disclosure the melt index of the second polyethylene I₂ ² may be from about 0.01 dg/min to about 1000 dg/min, or from about 0.01 dg/min to about 500 dg/min, or from about 0.01 dg/min to about 100 dg/min, or from about 0.01 dg/min to about 50 dg/min, or from about 0.1 dg/min to about 100 dg/min, or from about 0.1 dg/min to about 75 dg/min, or from about 0.1 dg/min to about 50 dg/min, or from about 1 dg/min to about 50 dg/min, or from about 1 dg/min to about 40 dg/min, or from about 1 dg/min to about 30 dg/min, or from about 1 dg/min to about 25 dg/min, or from about 3 dg/min to about 25 dg/min, or from about 5 dg/min to about 20 dg/min.

In an embodiment of the disclosure, the second polyethylene has a weight average molecular weight, M_(w) of from about 10,000 to about 150,000, or from about 10,000 to about 125,000, or from about 15,000 to about 100,000, or from about 15,000 to about 90,000, or from about 15,000 to about 80,000 or from about 20,000 to about 75,000, or from about 25,000 to about 90,000, or from about 25,000 to about 80,000, or from about 25,000 to about 75,000.

In an embodiment of the disclosure, the weight average molecular weight of the second polyethylene is less than the weight average molecular weight of the first polyethylene.

In an embodiment of the disclosure, the weight average molecular weight of the second polyethylene is less than the weight average molecular weight of the third polyethylene.

In an embodiment of the disclosure, the weight average molecular weight of the second polyethylene is less than the weight average molecular weight of both the first polyethylene and the third polyethylene.

In embodiments of the disclosure, the upper limit on the weight percent (wt. %) of the second polyethylene in the polyethylene composition (i.e. the weight percent of the second polyethylene based on the total weight of the first, the second and the third polyethylene) may be about 80 wt. %, or about 75 wt. %, or about 70 wt. %, or about 65 wt. %, or about 60 wt. %, or about 55 wt. %, or about 50 wt. %, or about 45 wt. %, or about 40 wt. %. In embodiments of the disclosure, the lower limit on the wt. % of the second polyethylene in the polyethylene composition may be about 5 wt. %, or about 10 wt. %, or about 15 wt. %, or about 20 wt. %.

The Third Polyethylene

In an embodiment of the disclosure, the third polyethylene is made with a multi-site catalyst system, non-limiting examples of which include Ziegler-Natta catalysts and chromium catalysts, both of which are well known in the art.

In an embodiment of the disclosure, the third polyethylene is made with a Ziegler-Natta catalyst.

Ziegler-Natta catalyst systems are well known to those skilled in the art. A Ziegler-Natta catalyst may be an in-line Ziegler-Natta catalyst system or a batch Ziegler-Natta catalyst system. The term “in-line Ziegler-Natta catalyst system” refers to the continuous synthesis of a small quantity of an active Ziegler-Natta catalyst system and immediately injecting this catalyst into at least one continuously operating reactor, wherein the catalyst polymerizes ethylene and one or more optional α-olefins to form an ethylene polymer. The terms “batch Ziegler-Natta catalyst system” or “batch Ziegler-Natta procatalyst” refer to the synthesis of a much larger quantity of catalyst or procatalyst in one or more mixing vessels that are external to, or isolated from, the continuously operating solution polymerization process. Once prepared, the batch Ziegler-Natta catalyst system, or batch Ziegler-Natta procatalyst, is transferred to a catalyst storage tank. The term “procatalyst” refers to an inactive catalyst system (inactive with respect to ethylene polymerization); the procatalyst is converted into an active catalyst by adding an alkyl aluminum co-catalyst. As needed, the procatalyst is pumped from the storage tank to at least one continuously operating reactor, wherein an active catalyst polymerizes ethylene and one or more optional α-olefins to form a polyethylene. The procatalyst may be converted into an active catalyst in the reactor or external to the reactor, or on route to the reactor.

A wide variety of compounds can be used to synthesize an active Ziegler-Natta catalyst system. The following describes various compounds that may be combined to produce an active Ziegler-Natta catalyst system. Those skilled in the art will understand that the embodiments in this disclosure are not limited to the specific compounds disclosed.

An active Ziegler-Natta catalyst system may be formed from: a magnesium compound, a chloride compound, a metal compound, an alkyl aluminum co-catalyst and an aluminum alkyl. As will be appreciated by those skilled in the art, Ziegler-Natta catalyst systems may contain additional components; a non-limiting example of an additional component is an electron donor, e.g. amines or ethers.

A non-limiting example of an active in-line (or batch) Ziegler-Natta catalyst system can be prepared as follows. In the first step, a solution of a magnesium compound is reacted with a solution of a chloride compound to form a magnesium chloride support suspended in solution. Non-limiting examples of magnesium compounds include Mg(R¹)₂; wherein the R¹ groups may be the same or different, linear, branched or cyclic hydrocarbyl radicals containing 1 to 10 carbon atoms. Non-limiting examples of chloride compounds include R²Cl; wherein R² represents a hydrogen atom, or a linear, branched or cyclic hydrocarbyl radical containing 1 to 10 carbon atoms. In the first step, the solution of magnesium compound may also contain an aluminum alkyl. Non-limiting examples of aluminum alkyl include Al(R³)₃, wherein the R³ groups may be the same or different, linear, branched or cyclic hydrocarbyl radicals containing from 1 to 10 carbon atoms. In the second step a solution of the metal compound is added to the solution of magnesium chloride and the metal compound is supported on the magnesium chloride. Non-limiting examples of suitable metal compounds include M(X)_(n) or MO(X)_(n); where M represents a metal chosen from Group 4 through Group 8 of the Periodic Table, or mixtures of metals chosen from Group 4 through Group 8; O represents oxygen, and; X represents chloride or bromide; n is an integer from 3 to 6 that satisfies the oxidation state of the metal. Additional non-limiting examples of suitable metal compounds include Group 4 to Group 8 metal alkyls, metal alkoxides (which may be prepared by reacting a metal alkyl with an alcohol) and mixed-ligand metal compounds that contain a mixture of halide, alkyl and alkoxide ligands. In the third step a solution of an alkyl aluminum co-catalyst is added to the metal compound supported on the magnesium chloride. A wide variety of alkyl aluminum co-catalysts are suitable, as expressed by formula: Al(R ⁴)_(p)(OR⁹)_(q)(X)_(r) wherein the R⁴ groups may be the same or different, hydrocarbyl groups having from 1 to 10 carbon atoms; the OR⁹ groups may be the same or different, alkoxy or aryloxy groups wherein R⁹ is a hydrocarbyl group having from 1 to 10 carbon atoms bonded to oxygen; X is chloride or bromide, and; (p+q+r)=3, with the proviso that p is greater than 0. Non-limiting examples of commonly used alkyl aluminum co-catalysts include trimethyl aluminum, triethyl aluminum, tributyl aluminum, dimethyl aluminum methoxide, diethyl aluminum ethoxide, dibutyl aluminum butoxide, dimethyl aluminum chloride or bromide, diethyl aluminum chloride or bromide, dibutyl aluminum chloride or bromide and ethyl aluminum dichloride or dibromide.

The process described in the paragraph above, to synthesize an active in-line (or batch) Ziegler-Natta catalyst system, can be carried out in a variety of solvents; non-limiting examples of solvents include linear or branched C₅ to C₁₂ alkanes or mixtures thereof.

In an embodiment of the disclosure, the third polyethylene is an ethylene copolymer. Suitable alpha-olefins which may be copolymerized with ethylene to give the third polyethylene include 1-propene, 1-butene, 1-pentene, 1-hexene and 1-octene.

In an embodiment of the disclosure, the third polyethylene is an ethylene homopolymer.

In an embodiment of the disclosure, the third polyethylene is a heterogeneously branched ethylene copolymer.

In an embodiment of the disclosure, the third polyethylene is an ethylene/I-octene copolymer.

In embodiments of the disclosure, the third polyethylene has a molecular weight distribution, M_(w)/M_(n) of ≥2.3, or ≥2.3, or ≥2.5, or ≥2.5, or ≥2.7, or ≥2.7, or ≥2.9, or ≥2.9, or ≥3.0, or 3.0. In embodiments of the disclosure, the third polyethylene has a molecular weight distribution, M_(w)/M_(n) of from 2.3 to 6.5, or from 2.3 to 6.0, or from 2.3 to 5.5, or from 2.3 to 5.0, or from 2.3 to 4.5, or from 2.3 to 4.0, or from 2.5 to 6.0, or from 2.5 to 5.5, or from 2.5 to 5.0, or from 2.5 to 4.5, or from 2.5 to 4.0, or from 2.7 to 6.0, or from 2.7 to 5.5, or from 2.7 to 5.0, or from 2.7 to 4.5, or from 2.9 to 6.5, or from 2.9 to 6.0, or from 2.9 to 5.5, or from 2.9 to 5.0, or from 2.9 to 4.5.

In an embodiment of the disclosure, the third polyethylene has from 0 to 100 short chain branches per thousand carbon atoms (SCB_(PE-3)). In further embodiments, the third polyethylene has from 0 to 50 short chain branches per thousand carbon atoms (SCB_(PE-3)), or from 0 to 35 short chain branches per thousand carbon atoms (SCB_(PE-3)), or from 3 to 30 short chain branches per thousand carbon atoms (SCB_(PE-3)), or from 5 to 30 short chain branches per thousand carbon atoms (SCB_(PE-3)), or from 5 to 25 short chain branches per thousand carbon atoms (SCB_(PE-3)), or from 3 to 25 short chain branches per thousand carbon atoms (SCB_(PE-3)), or from 1 to 25 short chain branches per thousand carbon atoms (SCB_(PE-3)), or from 0.1 to 20 short chain branches per thousand carbon atoms (SCB_(PE-3)).

The short chain branching (i.e. the short chain branching per thousand carbons, SCB_(PE-3)), if present, is the branching due to the presence of alpha-olefin comonomer in the polethylene and will for example have two carbon atoms for a 1-butene comonomer, or four carbon atoms for a 1-hexene comonomer, or six carbon atoms for a 1-octene comonomer, etc.

In an embodiment of the disclosure, the number of short chain branches per thousand carbon atoms in the third polyethylene (SCB_(PE-3)) is greater than the number of short chain branches per thousand carbon atoms in the second polyethylene (SCB_(PE-2)).

In embodiments of the disclosure, the upper limit on the density, d3 of the third polyethylene may be about 0.975 g/cm³; in some cases, about 0.965 g/cm³ and; in other cases, about 0.955 g/cm³. In embodiments of the disclosure, the lower limit on the density, d3 of the third polyethylene may be about 0.855 g/cm³, in some cases about 0.865 g/cm³, and; in other cases, about 0.875 g/cm³.

In embodiments of the disclosure the density, d3 of the third polyethylene may be from about 0.875 g/cm³ to about 0.965 g/cm³, or from about 0.875 g/cm³ to about 0.960 g/cm³, or from about 0.875 g/cm³ to 0.950 g/cm³, or from about 0.865 g/cm³ to about 0.940 g/cm³, or from about 0.865 g/cm³ to about 0.936 g/cm³, or from about 0.865 g/cm³ to about 0.932 g/cm³, or from about 0.865 g/cm³ to about 0.926 g/cm³, or from about 0.865 g/cm³ to about 0.921 g/cm³, or from about 0.865 g/cm³ to about 0.918 g/cm³, or from about 0.875 g/cm³ to about 0.916 g/cm³, or from about 0.875 g/cm³ to about 0.916 g/cm³, or from about 0.865 g/cm³ to about 0.912 g/cm³, or from about 0.880 g/cm³ to about 0.912 g/cm³, or from about 0.890 g/cm³ to about 0.916 g/cm³, or from about 0.900 g/cm³ to about 0.916 g/cm³, or from about 0.880 g/cm³ to about 0.916 g/cm³, or from about 0.880 g/cm³ to about 0.918 g/cm³, or from about 0.880 g/cm³ to about 0.921 g/cm³, or from about 0.880 g/cm³ to about 0.926 g/cm³, or from about 0.880 g/cm³ to about 0.932 g/cm³, or from about 0.880 g/cm³ to about 0.936 g/cm³.

In an embodiment of the disclosure, the third polyethylene is an ethylene copolymer which has a composition distribution breadth index, CDBI₅₀ of 75 wt. % or less, or 70 wt. % or less. In further embodiments of the disclosure, the third polyethylene is an ethylene copolymer which has a CDBI₅₀ of 65 wt. % or less, or 60 wt. % or less, or 55 wt. % or less, or 50 wt. % or less, or 45 wt. % or less.

In embodiments of the disclosure the melt index of the third polyethylene I₂ ³ may be from about 0.01 dg/min to about 1000 dg/min, or from about 0.01 dg/min to about 500 dg/min, or from about 0.01 dg/min to about 100 dg/min, or from about 0.01 dg/min to about 50 dg/min, or from about 0.01 dg/min to about 25 dg/min, or from about 0.01 dg/min to about 10 dg/min, or from about 0.01 dg/min to about 5 dg/min, or from about 0.01 dg/min to about 3 dg/min, or from about 0.01 dg/min to about 1 dg/min, or less than about 5 dg/min, or less than about 3 dg/min, or less than about 1.0 dg/min, or less than about 0.75 dg/min, or less than about 0.50 dg/min.

In an embodiment of the disclosure, the third polyethylene has a weight average molecular weight, M_(w) of from about 50,000 to about 300,000, or from about 50,000 to about 250,000, or from about 60,000 to about 250,000, or from about 70,000 to about 250,000, or from about 75,000 to about 200,000, or from about 80,000 to about 275,000; or from about 80,000 to about 250,000, or from about 80,000 to about 200,000, or from 70,000 to about 200,000, or from about 80,000 to about 175,000.

In an embodiment of the disclosure, the third polyethylene has a weight average molecular weight, M_(w) which is greater than the weight average molecular weight, M_(w) of the first polyethylene.

In an embodiment of the disclosure, the third polyethylene has a weight average molecular weight, M_(w) which is greater than the weight average molecular weight, M_(w) of the second polyethylene.

In embodiments of the disclosure, the upper limit on the weight percent (wt. %) of the third polyethylene in the polyethylene composition (i.e. the weight percent of the third polyethylene based on the total weight of the first, the second and the third polyethylene) may be about 90 wt. %, or about 85 wt. %, or about 80 wt. %, or about 75 wt. %, or 65 wt. %, in other cases about 60 wt. %, in other cases about 55 wt. %, or about 50 wt. %, or about 45 wt. %. In embodiments of the disclosure, the lower limit on the wt. % of the third polyethylene in the final polyethylene product may be about 5 wt. %, or about 10 wt. %, or about 15 wt. %, or about 20 wt. %, or about 25 wt. %, or about 30 wt. %, or about 35 wt. %, or in other cases about 40 wt. %.

In an embodiments of the disclosure, third polyethylene has no long chain branching present or does not have any detectable levels of long chain branching.

The Polyethylene Composition

The polyethylene compositions disclosed herein can be made using any well-known techniques in the art, including but not limited to melt blending, solution blending, or in-reactor blending to bring together a first polyethylene, a second polyethylene and a third polyethylene.

In an embodiment, the polyethylene composition of the present disclosure is made by melt blending or solution blending three different polyethylene components: i) a first polyethylene, ii) a second polyethylene, and iii) a third polyethylene.

In an embodiment, the polyethylene composition of the present disclosure is made by melt blending or solution blending two different polyethylene components: i) a first polyethylene component including a first polyethylene and a second polyethylene, and ii) second polyethylene component including a third polyethylene.

In an embodiment, the polyethylene composition of the present disclosure is made by melt blending or solution blending two different polyethylene components: i) a first polyethylene component including a first polyethylene and ii) a second polyethylene component including a second polyethylene and a third polyethylene.

In an embodiment, the polyethylene composition of the present disclosure is made by melt blending or solution blending two different polyethylene components: i) a first polyethylene component including a first polyethylene and a third polyethylene, and ii) a second polyethylene component including a second polyethylene.

In an embodiment, the polyethylene composition of the present disclosure is made using the same single site catalyst in two different reactors, where each reactor is operated under different polymerization conditions to give a first polyethylene and a second polyethylene and using a multi-site catalyst in another reactor to give the third polyethylene.

In an embodiment, the polyethylene composition of the present disclosure is made using a different single site catalyst in two different reactors, where each reactor is operated under similar or different polymerization conditions to give a first polyethylene and a second polyethylene, and using a multi-site catalyst in another reactor to give the third polyethylene.

It is also contemplated by the present disclosure, that the polymer compositions including a first, second and third polyethylene could be made in one or more polymerization reactor, using two different single site polymerization catalysts and a multi-site polymerization catalyst, where each catalyst has a different response to one or more of hydrogen concentration, ethylene concentration, comonomer concentration, and temperature under a given set of polymerization conditions, so that the first polyethylene is produced by the first single site catalyst, the second polyethylene is produced by the second single site catalyst, and the third polyethylene is produced by the multi-site catalyst.

It is also contemplated by the present disclosure, that the polymer compositions including a first, second and third polyethylene could be made in one or more polymerization reactors, using one or more single site polymerization catalysts, and one multi-site catalyst, where each catalyst has a similar or different response to one or more of hydrogen concentration, ethylene concentration, comonomer concentration, and temperature under a given set of polymerization conditions, and where one or more of hydrogen concentration, ethylene concentration, comonomer concentration, and temperature are cycled through a range so that a first, second and a third polyethylene is produced by the one or more single site catalysts and the one multi-site catalyst present in the one or more polymerization reactors.

In an embodiment, the polyethylene composition of the present disclosure is made by forming a first polyethylene in a first reactor by polymerizing ethylene and an alpha olefin with a single site catalyst; forming a second polyethylene in a second reactor by polymerizing ethylene and optionally an alpha olefin with a single site catalyst, and forming a third polyethylene in a third reactor by polymerizing ethylene and optionally an alpha olefin with a multi-site catalyst.

In an embodiment, the polyethylene composition of the present disclosure is made by forming a first polyethylene in a first reactor by polymerizing ethylene and an alpha olefin with a single site catalyst; forming a second polyethylene in a second reactor by polymerizing ethylene and optionally an alpha olefin with a single site catalyst, and forming a third polyethylene in a third reactor by polymerizing ethylene and optionally an alpha olefin with a multi-site catalyst, where at least two of the first, second and third reactors are configured in series with one another.

In an embodiment, the polyethylene composition of the present disclosure is made by forming a first polyethylene in a first solution phase polymerization reactor by polymerizing ethylene and an alpha olefin with a single site catalyst; forming a second polyethylene in a second solution phase polymerization reactor by polymerizing ethylene and optionally an alpha olefin with a single site catalyst, and forming a third polyethylene in a third solution phase polymerization reactor by polymerizing ethylene and optionally an alpha olefin with a multi-site catalyst.

In an embodiment, the polyethylene composition of the present disclosure is made by forming a first polyethylene in a first solution phase polymerization reactor by polymerizing ethylene and an alpha olefin with a single site catalyst; forming a second polyethylene in a second solution phase polymerization reactor by polymerizing ethylene and optionally an alpha olefin with a single site catalyst, and forming a third polyethylene in a third solution phase polymerization reactor by polymerizing ethylene and optionally an alpha olefin with a multi-site catalyst, where at least two of the first, second and third solution phase polymerization reactors are configured in series with one another.

In an embodiment, the polyethylene composition of the present disclosure is made by forming a first polyethylene in a first solution phase polymerization reactor by polymerizing ethylene and an alpha olefin with a single site catalyst; forming a second polyethylene in a second solution phase polymerization reactor by polymerizing ethylene and optionally an alpha olefin with a single site catalyst, and forming a third polyethylene in a third solution phase polymerization reactor by polymerizing ethylene and optionally an alpha olefin with a multi-site catalyst, where the first and second solution phase polymerization reactors are configured in series with one another.

In an embodiment, the polyethylene composition of the present disclosure is made by forming a first polyethylene in a first reactor by polymerizing ethylene and an alpha olefin with a single site catalyst; forming a second polyethylene in a second reactor by polymerizing ethylene and optionally an alpha olefin with a single site catalyst, and forming a third polyethylene in a third reactor by polymerizing ethylene and optionally an alpha olefin with a multi-site catalyst, where each of the first, second and third reactors are configured in parallel to one another.

In an embodiment, the polyethylene composition of the present disclosure is made by forming a first polyethylene in a first solution phase polymerization reactor by polymerizing ethylene and an alpha olefin with a single site catalyst; forming a second polyethylene in a second solution phase polymerization reactor by polymerizing ethylene and optionally an alpha olefin with a single site catalyst, and forming a third polyethylene in a third solution phase polymerization reactor by polymerizing ethylene and optionally an alpha olefin with a multi-site catalyst, where each of the first, second and third solution phase polymerization reactors are configured in parallel to one another.

In an embodiment, the polyethylene composition of the present disclosure is made by forming a first polyethylene in a first reactor by polymerizing ethylene and an alpha olefin with a single site catalyst; forming a second polyethylene in a second reactor by polymerizing ethylene and optionally an alpha olefin with a single site catalyst, and forming a third polyethylene in a third reactor by polymerizing ethylene and optionally an alpha olefin with a multi-site catalyst, where the first and second reactors are configured in series to one another, and the third reactor is configured in parallel to the first and second reactors.

In an embodiment, the polyethylene composition of the present disclosure is made by forming a first polyethylene in a first solution phase reactor by polymerizing ethylene and an alpha olefin with a single site catalyst; forming a second polyethylene in a second solution phase reactor by polymerizing ethylene and optionally an alpha olefin with a single site catalyst, and forming a third polyethylene in a third solution phase reactor by polymerizing ethylene and optionally an alpha olefin with a multi-site catalyst, where the first and second solution phase reactors are configured in series to one another, and the third solution phase reactor is configured in parallel to the first and second reactors.

In an embodiment, the solution phase polymerization reactor used as a first solution phase reactor, a second solution phase reactor, or a third solution phase reactor is a continuously stirred tank reactor.

In an embodiment, the solution phase polymerization reactor used as a first solution phase reactor, a second solution phase reactor, or a third solution phase reactor is a tubular reactor.

In a solution phase polymerization reactor, a variety of solvents may be used as the process solvent; non-limiting examples include linear, branched or cyclic C₅ to C₁₂ alkanes. Non-limiting examples of α-olefins include 1-propene, 1-butene, 1-pentene, 1-hexene and 1-octene. Suitable catalyst component solvents include aliphatic and aromatic hydrocarbons. Non-limiting examples of aliphatic catalyst component solvents include linear, branched or cyclic C₅-12 aliphatic hydrocarbons, e.g. pentane, methyl pentane, hexane, heptane, octane, cyclohexane, cyclopentane, methylcyclohexane, hydrogenated naphtha or combinations thereof. Non-limiting examples of aromatic catalyst component solvents include benzene, toluene (methylbenzene), ethylbenzene, o-xylene (1,2-dimethylbenzene), m-xylene (1,3-dimethylbenzene), p-xylene (1,4-dimethylbenzene), mixtures of xylene isomers, hemellitene (1,2,3-trimethylbenzene), pseudocumene (1,2,4-trimethylbenzene), mesitylene (1,3,5-trimethylbenzene), mixtures of trimethylbenzene isomers, prehenitene (1,2,3,4-tetramethylbenzene), durene (1,2,3,5-tetramethylbenzene), mixtures of tetramethylbenzene isomers, pentamethylbenzene, hexamethylbenzene and combinations thereof.

In embodiments of the disclosure, the polyethylene composition has a density which may be from about 0.880 g/cm³ to about 0.965 g/cm³, or from about 0.885 g/cm³ to about 0.960 g/cm³, or from about 0.890 g/cm³ to 0.950 g/cm³, or from about 0.895 g/cm³ to about 0.940 g/cm³, or from about 0.900 g/cm³ to about 0.936 g/cm³, or from about 0.905 g/cm³ to about 0.934 g/cm³, or from about 0.910 g/cm³ to about 0.932 g/cm³, or from about 0.910 g/cm³ to about 0.930 g/cm³, or from about 0.910 g/cm³ to about 0.926 g/cm³, or from about 0.890 g/cm³ to about 0.924 g/cm³, or from about 0.890 g/cm³ to about 0.922 g/cm³, or from about 0.890 g/cm³ to about 0.920 g/cm³, or from about 0.890 g/cm³ to about 0.918 g/cm³, or from about 0.880 g/cm³ to about 0.922 g/cm³, or from about 0.880 g/cm³ to about 0.926 g/cm³, or from about 0.880 g/cm³ to about 0.932 g/cm³, or ≤0.948 g/cm³, or <0.948 g/cm³, or ≤0.945 g/cm³, or <0.945 g/cm³, or ≤0.940 g/cm³, or <0.940 g/cm³, or ≤0.939 g/cm³, or <0.939 g/cm³, or ≤0.935 g/cm³, or <0.935 g/cm³, or ≤0.932 g/cm³, or <0.932 g/cm³.

In embodiments of the disclosure the melt index I₂ of the polyethylene composition may be from about 0.01 dg/min to about 1000 dg/min, or from about 0.01 dg/min to about 500 dg/min, or from about 0.01 dg/min to about 100 dg/min, or from about 0.01 dg/min to about 50 dg/min, or from about 0.01 dg/min to about 25 dg/min, or from about 0.01 dg/min to about 10 dg/min, or from about 0.01 dg/min to about 5 dg/min, or from about 0.01 dg/min to about 3 dg/min, or from about 0.01 dg/min to about 1 dg/min, or from about 0.1 dg/min to about 10 dg/min, or from about 0.1 dg/min to about 5 dg/min, or from about 0.1 dg/min to about 3 dg/min, or from about 0.1 dg/min to about 2 dg/min, or from about 0.1 dg/min to about 1.5 dg/min, or from about 0.1 dg/min to about 1 dg/min, or less than about 5 dg/min, or less than about 3 dg/min, or less than about 1.0 dg/min.

In embodiments of the disclosure the high load melt index I₂₁ of the polyethylene composition may be from about 15 dg/min to about 10,000 dg/min, or from about 15 dg/min to about 1000 dg/min, or from about 15 dg/min to about 100 dg/min, or from about 15 dg/min to about 75 dg/min, or from about 15 dg/min to about 50 dg/min, or from about 10 dg/min to about 100 dg/min, or from about 10 dg/min to about 75 dg/min, or from about 10 dg/min to about 50 dg/min, or from about 10 dg/min to about 45 dg/min, or from about 10 dg/min to about 40 dg/min, or from about 10 dg/min to about 35 dg/min, or from about 10 dg/min to about 32 dg/min, or from about 10 dg/min to about 36 dg/min.

In an embodiment of the disclosure the melt flow ratio I₂₁/I₂ of the polyethylene composition is ≤40. In embodiments of the disclosure the melt flow ratio I₂₁/I₂ of the polyethylene composition may be from about 15 to about 40, or from about 15 to about 38, or from about 18 to about 40, or from about 20 to about 40, or from about 25 to about 40, or from about 28 to about 40.

In an embodiments of the disclosure, the polyethylene composition has a weight average molecular weight, M_(w) of from about 50,000 to about 300,000, or from about 50,000 to about 250,000, or from about 60,000 to about 250,000, or from about 70,000 to about 225,000, or from about 70,000 to about 200,000, or from about 75,000 to about 175,000, or from about 75,000 to about 150,000, or from about 100,000 to about 130,000.

In embodiments of the disclosure, the polyethylene composition has a lower limit molecular weight distribution, M_(w)/M_(n) of 2.0, or 2.1, or 2.3, or 2.5. In embodiments of the disclosure, the polyethylene composition has an upper limit molecular weight distribution, M_(w)/M_(n) of 6.0, or 5.5, or 5.0, or 4.5, or 4.0, or 3.5, or 3.0. In embodiments of the disclosure, the polyethylene composition has a molecular weight distribution, M_(w)/M_(n) of from 2.1 to 6.0, or from 2.3 to 6.0, or from 2.5 to 6.0, or from 2.1 to 5.5, or from 2.3 to 5.5, or from 2.1 to 5.0, or from 2.3 to 5.0, or from 2.1 to 4.5, or from 2.3 to 4.5, or from 2.1 to 4.0, or from 2.3 to 4.0, or from 2.1 to 3.5, or from 2.3 to 3.5, or from 2.1 to 3.0, or from 2.3 to 3.0.

In embodiments of the disclosure, the polyethylene composition has a Z-average molecular weight distribution, M_(Z)/M_(W) of ≤4.0, or <4.0, or ≤3.5, or <3.5, or ≤3.0, or <3.0, or ≤2.75, or <2.75, or ≤2.50, or <2.50. In embodiments of the disclosure, the polyethylene composition has a Z-average molecular weight distribution, M_(Z)/M_(W) of from 1.5 to 4.0, or from 1.75 to 3.5, or from 1.75 to 3.0, or from 2.0 to 4.0, or from 2.0 to 3.5, or from 2.0 to 3.0, or from 2.0 to 2.5.

In an embodiment of the disclosure, the polyethylene composition has a unimodal profile in a gel permeation chromatograph generated according to the method of ASTM D6474-99. The term “unimodal” is herein defined to mean there will be only one significant peak or maximum evident in the GPC-curve. A unimodal profile includes a broad unimodal profile. In contrast, the use of the term “bimodal” is meant to convey that in addition to a first peak, there will be a secondary peak or shoulder which represents a higher or lower molecular weight component (i.e. the molecular weight distribution, can be said to have two maxima in a molecular weight distribution curve). Alternatively, the term “bimodal” connotes the presence of two maxima in a molecular weight distribution curve generated according to the method of ASTM D6474-99. The term “multi-modal” denotes the presence of two or more, typically more than two, maxima in a molecular weight distribution curve generated according to the method of ASTM D6474-99.

In an embodiment of the disclosure the polyethylene composition may have a multimodal profile in a differential scanning calorimetry (DSC) graph. In the context of DSC analysis, the term “multimodal” connotes a DSC profile in which two or more distinct melting peaks are observable.

In an embodiment of the disclosure the polyethylene composition may have a bimodal profile in a differential scanning calorimetry (DSC) graph. In the context of DSC analysis, the term “bimodal” connotes a DSC profile in which two distinct melting peaks are observable.

In an embodiment of the disclosure, the polyethylene composition has a melting peak temperature in a differential scanning calorimetry (DSC) analysis at above 120° C. For clarity sake, by the phrase “has a melting peak temperature in an DSC analysis” it is meant that in a DSC analysis, although there may be one or more melting peaks evident, at least one such peak occurs at above the indicated temperature. In an embodiment of the disclosure, the polyethylene composition has a melting peak temperature in a differential scanning calorimetry (DSC) analysis at above 123° C. In an embodiment of the disclosure, the polyethylene composition has a melting peak temperature in a differential scanning calorimetry (DSC) analysis at above 125° C.

In an embodiment of the disclosure, the polyethylene composition will have a reverse or partially reverse comonomer distribution profile as measured using GPC-FTIR. If the comonomer incorporation decreases with molecular weight, as measured using GPC-FTIR, the distribution is described as “normal”. If the comonomer incorporation is approximately constant with molecular weight, as measured using GPC-FTIR, the comonomer distribution is described as “flat” or “uniform”. The terms “reverse comonomer distribution” and “partially reverse comonomer distribution” mean that in the GPC-FTIR data obtained for a copolymer, there is one or more higher molecular weight components having a higher comonomer incorporation than in one or more lower molecular weight components. The term “reverse(d) comonomer distribution” is used herein to mean, that across the molecular weight range of an ethylene copolymer, comonomer contents for the various polymer fractions are not substantially uniform and the higher molecular weight fractions thereof have proportionally higher comonomer contents (i.e. if the comonomer incorporation rises with molecular weight, the distribution is described as “reverse” or “reversed”). Where the comonomer incorporation rises with increasing molecular weight and then declines, the comonomer distribution is still considered “reverse”, but may also be described as “partially reverse”. A partially reverse comonomer distribution will exhibit a peak or maximum.

In an embodiment of the disclosure the polyethylene composition has a reversed comonomer distribution profile as measured using GPC-FTIR.

In an embodiment of the disclosure the polyethylene composition has a partially reversed comonomer distribution profile as measured using GPC-FTIR.

In an embodiment of the disclosure, the polyethylene composition has a soluble fraction of at least 10 wt. % in a crystallization elution fractionation (CEF) analysis, where the soluble fraction is defined as the weight percent (wt. %) of material which elutes at 30° C. and below. In an embodiment of the disclosure, the polyethylene composition has a soluble fraction of at least 15 wt. % in a crystallization elution fractionation (CEF) analysis, where the soluble fraction is defined as the weight percent (wt. %) of material which elutes at 30° C. and below. In an embodiment of the disclosure, the polyethylene composition has a soluble fraction of at least 17 wt. % in a crystallization elution fractionation (CEF) analysis, where the soluble fraction is defined as the weight percent (wt. %) of material which elutes at 30° C. and below. In an embodiment of the disclosure, the polyethylene composition has a soluble fraction of at least 20 wt. % in a crystallization elution fractionation (CEF) analysis, where the soluble fraction is defined as the weight percent (wt. %) of material which elutes at 30° C. and below. In an embodiment of the disclosure, the polyethylene composition has a soluble fraction of at least 25 wt. % in a crystallization elution fractionation (CEF) analysis, where the soluble fraction is defined as the weight percent (wt. %) of material which elutes at 30° C. and below. In an embodiment of the disclosure, the polyethylene composition has a soluble fraction of from 10 to 40 wt. % in a crystallization elution fractionation (CEF) analysis, where the soluble fraction is defined as the weight percent (wt. %) of material which elutes at 30° C. and below. In an embodiment of the disclosure, the polyethylene composition has a soluble fraction of from 15 to 35 wt. % in a crystallization elution fractionation (CEF) analysis, where the soluble fraction is defined as the weight percent (wt. %) of material which elutes at 30° C. and below.

In an embodiment of the disclosure, the polyethylene composition has a stress exponent, defined as Log₁₀[I₆/I₂]/Log₁₀[6.48/2.16], which is ≤1.50. In further embodiments of the disclosure the polyethylene composition has a stress exponent, Log₁₀[I₆/I₂]/Log₁₀[6.48/2.16] of less than 1.48, or less than 1.45, or less than 1.43.

In an embodiment of the disclosure, the polyethylene composition has a hexane extractable value of ≤5.0 weight percent, or less than 4.0 wt. %, or less than 3.0 wt. %, or less than 2.0 wt. %, or less than 1.0 wt. %.

The polyethylene composition disclosed herein may be converted into flexible manufactured articles such as monolayer or multilayer films, such films are well known to those experienced in the art; non-limiting examples of processes to prepare such films include blown film and cast film processes.

In the blown film extrusion process an extruder heats, melts, mixes and conveys a thermoplastic, or a thermoplastic blend. Once molten, the thermoplastic is forced through an annular die to produce a thermoplastic tube. In the case of co-extrusion, multiple extruders are employed to produce a multilayer thermoplastic tube. The temperature of the extrusion process is primarily determined by the thermoplastic or thermoplastic blend being processed, for example the melting temperature or glass transition temperature of the thermoplastic and the desired viscosity of the melt. In the case of polyolefins, typical extrusion temperatures are from 330° F. to 550° F. (166° C. to 288° C.). Upon exit from the annular die, the thermoplastic tube is inflated with air, cooled, solidified and pulled through a pair of nip rollers. Due to air inflation, the tube increases in diameter forming a bubble of desired size. Due to the pulling action of the nip rollers the bubble is stretched in the machine direction. Thus, the bubble is stretched in two directions: the transverse direction (TD) where the inflating air increases the diameter of the bubble; and the machine direction (MD) where the nip rollers stretch the bubble. As a result, the physical properties of blown films are typically anisotropic, i.e. the physical properties differ in the MD and TD directions; for example, film tear strength and tensile properties typically differ in the MD and TD. In some references, the terms “cross direction” or “CD” is used; these terms are equivalent to the terms “transverse direction” or “TD” used in this disclosure. In the blown film process, air is also blown on the external bubble circumference to cool the thermoplastic as it exits the annular die. The final width of the film is determined by controlling the inflating air or the internal bubble pressure; in other words, increasing or decreasing bubble diameter. Film thickness is controlled primarily by increasing or decreasing the speed of the nip rollers to control the draw-down rate. After exiting the nip rollers, the bubble or tube is collapsed and may be slit in the machine direction thus creating sheeting. Each sheet may be wound into a roll of film. Each roll may be further slit to create film of the desired width. Each roll of film is further processed into a variety of consumer products as described below.

The cast film process is similar in that a single or multiple extruder(s) may be used; however the various thermoplastic materials are metered into a flat die and extruded into a monolayer or multilayer sheet, rather than a tube. In the cast film process the extruded sheet is solidified on a chill roll.

Depending on the end-use application, the disclosed polyethylene composition may be converted into films that span a wide range of thicknesses. Non-limiting examples include, food packaging films where thicknesses may range from about 0.5 mil (13 μm) to about 4 mil (102 μm), and; in heavy duty sack applications film thickness may range from about 2 mil (51 μm) to about 10 mil (254 μm).

The polyethylene composition disclosed herein may be used in monolayer films; where the monolayer may contain more than one polyethylene composition and/or additional thermoplastics; non-limiting examples of thermoplastics include polyethylene polymers and propylene polymers. The lower limit on the weight percent of the polyethylene composition in a monolayer film may be about 3 wt. %, in other cases about 10 wt. % and in still other cases about 30 wt. %. The upper limit on the weight percent of the polyethylene composition in the monolayer film may be 100 wt. %, in other cases about 90 wt. % and in still other cases about 70 wt. %.

The polyethylene composition disclosed herein may also be used in one or more layers of a multilayer film; non-limiting examples of multilayer films include three, five, seven, nine, eleven or more layers. The thickness of a specific layer (containing the polyethylene composition) within a multilayer film may be about 5%, in other cases about 15% and in still other cases about 30% of the total multilayer film thickness. In other embodiments, the thickness of a specific layer (containing the polyethylene composition) within a multilayer film may be about 95%, in other cases about 80% and in still other cases about 65% of the total multilayer film thickness. Each individual layer of a multilayer film may contain more than one polyethylene composition and/or additional thermoplastics.

Additional embodiments include laminations and coatings, wherein mono or multilayer films containing the disclosed polyethylene composition are extrusion laminated or adhesively laminated or extrusion coated. In extrusion lamination or adhesive lamination, two or more substrates are bonded together with a thermoplastic or an adhesive, respectively. In extrusion coating, a thermoplastic is applied to the surface of a substrate. These processes are well known to those experienced in the art. Frequently, adhesive lamination or extrusion lamination are used to bond dissimilar materials, non-limiting examples include the bonding of a paper web to a thermoplastic web, or the bonding of an aluminum foil containing web to a thermoplastic web, or the bonding of two thermoplastic webs that are chemically incompatible, e.g. the bonding of a polyethylene composition containing web to a polyester or polyamide web. Prior to lamination, the web containing the disclosed polyethylene composition(s) may be monolayer or multilayer. Prior to lamination the individual webs may be surface treated to improve the bonding, a non-limiting example of a surface treatment is corona treating. A primary web or film may be laminated on its upper surface, its lower surface, or both its upper and lower surfaces with a secondary web. A secondary web and a tertiary web could be laminated to the primary web; wherein the secondary and tertiary webs differ in chemical composition. As non-limiting examples, secondary or tertiary webs may include; polyamide, polyester and polypropylene, or webs containing barrier resin layers such as EVOH. Such webs may also contain a vapor deposited barrier layer; for example, a thin silicon oxide (SiO_(x)) or aluminum oxide (AlO_(x)) layer. Multilayer webs (or films) may contain three, five, seven, nine, eleven or more layers.

The polyethylene composition disclosed herein can be used in a wide range of manufactured articles including one or more films or film layers (monolayer or multilayer). Non-limiting examples of such manufactured articles include: food packaging films (fresh and frozen foods, liquids and granular foods), stand-up pouches, retortable packaging and bag-in-box packaging; barrier films (oxygen, moisture, aroma, oil, etc.) and modified atmosphere packaging; light and heavy duty shrink films and wraps, collation shrink film, pallet shrink film, shrink bags, shrink bundling and shrink shrouds; light and heavy duty stretch films, hand stretch wrap, machine stretch wrap and stretch hood films; high clarity films; heavy-duty sacks; household wrap, overwrap films and sandwich bags; industrial and institutional films, trash bags, can liners, magazine overwrap, newspaper bags, mail bags, sacks and envelopes, bubble wrap, carpet film, furniture bags, garment bags, coin bags, auto panel films; medical applications such as gowns, draping and surgical garb; construction films and sheeting, asphalt films, insulation bags, masking film, landscaping film and bags; geomembrane liners for municipal waste disposal and mining applications; batch inclusion bags; agricultural films, mulch film and green house films; in-store packaging, self-service bags, boutique bags, grocery bags, carry-out sacks and t-shirt bags; oriented films, machine direction and biaxially oriented films and functional film layers in oriented polypropylene (OPP) films, e.g. sealant and/or toughness layers. Additional manufactured articles including one or more films containing at least one polyethylene composition include laminates and/or multilayer films; sealants and tie layers in multilayer films and composites; laminations with paper; aluminum foil laminates or laminates containing vacuum deposited aluminum; polyamide laminates; polyester laminates; extrusion coated laminates, and; hot-melt adhesive formulations. The manufactured articles summarized in this paragraph contain at least one film (monolayer or multilayer) including at least one embodiment of the disclosed polyethylene composition.

Desired film physical properties (monolayer or multilayer) typically depend on the application of interest. Non-limiting examples of desirable film properties include: optical properties (gloss, haze and clarity), dart impact, Elmendorf tear, modulus (1% and 2% secant modulus), puncture-propagation tear resistance, tensile properties (yield strength, break strength, elongation at break, toughness, etc.) and heat sealing properties (heat seal initiation temperature and hot tack strength). Specific hot tack and heat sealing properties are desired in high speed vertical and horizontal form-fill-seal processes that load and seal a commercial product (liquid, solid, paste, part, etc.) inside a pouch-like package.

In addition to desired film physical properties, it is desired that the disclosed polyethylene composition is easy to process on film lines. Those skilled in the art frequently use the term “processability” to differentiate polymers with improved processability, relative to polymers with inferior processability. A commonly used measure to quantify processability is extrusion pressure; for example, a polymer with improved processability has a lower extrusion pressure (on a blown film or a cast film extrusion line) relative to a polymer with inferior processability.

In an embodiment of the disclosure, a film or film layer includes the polyethylene composition described above.

In embodiments of the disclosure, a film or film layer includes the polyethylene composition described above and has a thickness of from 0.5 to 10 mil.

In embodiments of the disclosure, a film or film layer has a thickness of from 0.5 to 10 mil.

In embodiments of the disclosure, a film will have a dart impact strength of ≥400 g/mil, or ≥450 g/mil, or ≥500 g/mil, or ≥600 g/mil, or ≥700 g/mil. In another embodiment of the disclosure, a film will have a dart impact strength of from 400 g/mil to 950 g/mil. In a further embodiment of the disclosure, a film will have dart impact strength of from 400 g/mil to 850 g/mil. In a further embodiment of the disclosure, a film will have dart impact strength of from 500 g/mil to 900 g/mil. In a further embodiment of the disclosure, a film will have dart impact strength of from 550 g/mil to 850 g/mil. In yet another embodiment of the disclosure, the film will have dart impact strength of from 600 g/mil to 850 g/mil. In still yet another embodiment of the disclosure, a film will have dart impact strength of from 600 g/mil to 800 g/mil.

In embodiments of the disclosure, a 1 mil film will have a machine direction (MD) secant modulus at 1% strain of ≥150 MPa, or ≥160 MPa, or ≥170 MPa, or ≥180 MPa, or ≥190 MPa, or ≥200 MPa. In another embodiment of the disclosure, a 1 mil film will have a machine direction (MD) secant modulus at 1% strain of from 150 MPa to 280 MPa. In an embodiment of the disclosure, a 1 mil film will have a machine direction (MD) secant modulus at 1% strain of from 160 MPa to 260 MPa. In an embodiment of the disclosure, a 1 mil film will have a machine direction (MD) secant modulus at 1% strain of from 170 MPa to 250 MPa. In another embodiment of the disclosure, a 1 mil film will have a machine direction (MD) secant modulus at 1% strain of from 180 MPa to 240 MPa. In another embodiment of the disclosure, a 1 mil film will have a machine direction (MD) secant modulus at 1% strain of from 180 MPa to 230 MPa.

In an embodiment of the disclosure, a 1 mil film will have a transverse direction (TD) secant modulus at 1% strain of ≥190 MPa, or ≥200 MPa, or ≥210 MPa, or ≥220 MPa, or ≥230 MPa. In an embodiment of the disclosure, a 1 mil film will have a transverse direction (TD) secant modulus at 1% strain of from 160 MPa to 300 MPa. In another embodiment of the disclosure, a 1 mil film will have a transverse direction (TD) secant modulus at 1% strain of from 160 MPa to 280 MPa. In another embodiment of the disclosure, a 1 mil film will have a transverse direction (TD) secant modulus at 1% strain of from 170 MPa to 290 MPa. In another embodiment of the disclosure, a 1 mil film will have a transverse direction (TD) secant modulus at 1% strain of from 180 MPa to 290 MPa. In another embodiment of the disclosure, a 1 mil film will have a transverse direction (TD) secant modulus at 1% strain of from 190 MPa to 280 MPa. In another embodiment of the disclosure, a 1 mil film will have a transverse direction (TD) secant modulus at 1% strain of from 190 MPa to 270 MPa.

In embodiments of the disclosure, a 1 mil film will have a machine direction (MD) tensile strength at break of ≥40 MPa, or ≥45 MPa, or ≥50 MPa. In an embodiment of the disclosure, a 1 mil film will have a machine direction tensile strength at break of from 30 MPa to 70 MPa. In an embodiment of the disclosure, a 1 mil film will have a machine direction (MD) tensile strength at break of from 35 MPa to 70 MPa. In another embodiment of the disclosure, a 1 mil film will have a machine direction (MD) tensile strength at break of from 40 MPa to 70 MPa.

In embodiments of the disclosure, a film will have a machine direction (MD) tear strength of ≥160 g/mil, or ≤170 g/mil, or ≥180 g/mil, or ≥190 g/mil, or ≥200 g/mil, or ≥210 g/mil, or ≥220 g/mil, or ≥230 g/mil, or ≥240 g/mil, or ≥250 g/mil. In an embodiment of the disclosure, a film will have a machine direction (MD) tear strength of from 150 g/mil to 320 g/mil. In an embodiment of the disclosure, a film will have a machine direction (MD) tear strength of from 160 g/mil to 320 g/mil. In an embodiment of the disclosure, a film will have a machine direction (MD) tear strength of from 160 g/mil to 310 g/mil. In an embodiment of the disclosure, a film will have a machine direction (MD) tear strength of from 170 g/mil to 300 g/mil.

In embodiments of the disclosure, a 1 mil film will have a slow puncture resistance value of ≥45 J/mm, or ≥50 J/mm, or ≥55 J/mm. In embodiments of the disclosure, a 1 mil film will have a slow puncture value of from 40 J/mm to 90 J/mm, or from 50 J/mm to 90 J/mm, or from 50 J/mm to 80 J/mm.

In embodiments of the disclosure, a 1 mil film will have a haze of ≤25%, or ≤23%, ≤20%, or ≤15%. In embodiments of the disclosure, a 1 mil film will have a haze of from 7% to 25%, or from 8% to 23%.

In embodiments of the disclosure, a 2 mil film will have a seal initiation temperature (SIT) of ≤100° C., or ≤95° C., or ≤90° C., or ≤85° C. In an embodiment of the disclosure, a 2 mil film will have a seal initiation temperature (SIT) of between 65° C. and 100° C. In an embodiment of the disclosure, a 2 mil film will have a seal initiation temperature (SIT) of between 75° C. and 100° C. In an embodiment of the disclosure, a 2 mil film will have a seal initiation temperature (SIT) of between 75° C. and 95° C. In an embodiment of the disclosure, a 2 mil film will have a seal initiation temperature (SIT) of between 80° C. and 95° C.

In an embodiment of the disclosure, a 1 mil film will have an oxygen transmission rate (OTR) of ≥600 cm³ per 100 inch² per day. In an embodiment of the disclosure, a 1 mil film will have an oxygen transmission rate (OTR) of ≥650 cm³ per 100 inch² per day. In an embodiment of the disclosure, a 1 mil film will have an oxygen transmission rate (OTR) of ≥700 cm³ per 100 inch² per day. In an embodiment of the disclosure, a 1 mil film will have an oxygen transmission rate (OTR) of ≥740 cm³ per 100 inch² per day. In an embodiment of the disclosure, a 1 mil film will have an oxygen transmission rate (OTR) of ≥800 cm³ per 100 inch² per day. In an embodiment of the disclosure, a 1 mil film will have an oxygen transmission rate (OTR) of from 600 to 900 cm³ per 100 inch² per day. In an embodiment of the disclosure, a 1 mil film will have an oxygen transmission rate (OTR) of from 650 to 900 cm³ per 100 inch² per day. In an embodiment of the disclosure, a 1 mil film will have an oxygen transmission rate (OTR) of from 700 to 900 cm³ per 100 inch per day.

In an embodiment of the disclosure, a 2 mil film will have an area of hot tack window (AHTW) of ≥160 Newtons·° C. In an embodiment of the disclosure, a 2 mil film will have an area of hot tack window (AHTW) of ≥170 Newtons·° C. In an embodiment of the disclosure, a 2 mil film will have an area of hot tack window (AHTW) of ≥180 Newtons·° C. In an embodiment of the disclosure, a 2 mil film will have an area of hot tack window (AHTW) of from 160 to 260 Newtons·° C. In an embodiment of the disclosure, a 2 mil film will have an area of hot tack window (AHTW) of from 160 to 240 Newtons·° C. In an embodiment of the disclosure, a 2 mil film will have an area of hot tack window (AHTW) of from 160 to 230 Newtons·° C. In an embodiment of the disclosure, a 2 mil film will have an area of hot tack window (AHTW) of from 170 to 220 Newtons·° C. In an embodiment of the disclosure, a 2 mil film will have an area of hot tack window (AHTW) of from 170 to 200 Newtons·° C.

Some embodiments of the present disclosure provide films with improvements in machine direction (MD) modulus (1% and/or 2%) and seal initiation temperature relative to films formed from comparative polyethylene. Hence, in an embodiment of the disclosure, a film layer having a thickness of from 0.5 to 10 mil, has a machine direction (MD) 1% secant modulus of ≥180 MPa when measured at a film thickness of about 1 mil and a seal initiation temperature (SIT) of ≤100° C. when measured at a film thickness of about 2 mil. In another embodiment of the disclosure, a film layer having a thickness of from 0.5 to 10 mil, has a machine direction (MD) 1% secant modulus of ≥190 MPa when measured at a film thickness of about 1 mil and a seal initiation temperature (SIT) of ≤95° C. when measured at a film thickness of about 2 mil. In another embodiment of the disclosure, a film layer having a thickness of from 0.5 to 10 mil, has a machine direction (MD) 1% secant modulus of ≥200 MPa when measured at a film thickness of about 1 mil and a seal initiation temperature (SIT) of ≤95° C. when measured at a film thickness of about 2 mil.

Some embodiments of the present disclosure provide films with improvements in machine direction (MD) modulus (1% and/or 2%) and oxygen transmission rates (OTRs) relative to films formed from comparative polyethylene. Hence, in an embodiment of the disclosure, a film layer having a thickness of from 0.5 to 10 mil, has a machine direction (MD) 1% secant modulus of ≥190 MPa when measured at a film thickness of about 1 mil and an oxygen transmission rate (OTR) of ≥650 cm³ per 100 inch² per day when measured at a film thickness of about 1 mil.

In an embodiment of the disclosure, the films manufactured using the polyethylene compositions will have good hot tack performance. Good hot tack performance is generally associated with good film performance in bag or pouch packaging lines, such as vertical-form-fill-seal (VFFS) applications lines. Without wishing to be bound by theory, in the hot tack profile (seal temperature vs. force), good hot tack performance is indicated by an early (or low) hot tack initiation temperature, then a relatively high force over a wide range of seal temperatures.

Some embodiments of the present disclosure provide films with improvements in machine direction (MD) modulus (1% and/or 2%) and area of hot tack window (AHTW) relative to films formed from comparative polyethylene. Hence, in an embodiment of the disclosure, a film layer having a thickness of from 0.5 to 10 mil, has a machine direction (MD) 1% secant modulus of ≤190 MPa when measured at a film thickness of about 1 mil and an area of hot tack window (AHTW) of ≥160 Newtons·° C. when measured at a film thickness of about 2 mil.

Some embodiments of the present disclosure provide films with improvements in machine direction (MD) modulus (1% and/or 2%), oxygen transmission rates, seal initiation temperature and area of hot tack window (AHTW) relative to films formed from comparative polyethylene. Hence, in an embodiment of the disclosure, a film layer having a thickness of from 0.5 to 10 mil, has a has a machine direction (MD) 1% secant modulus of ≥190 MPa when measured at a film thickness of about 1 mil, an oxygen transmission rate (OTR) of ≥650 cm³ per 100 inch² per day when measured at a film thickness of about 1 mil, a seal initiation temperature (SIT) of ≤100° C. when measured at a film thickness of about 2 mil, and an area of hot tack window (AHTW) of ≥160 Newtons·® C. when measured at a film thickness of about 2 mil.

In an embodiment of the disclosure, film satisfies the following relationship: area of hot tack window (AHTW)>−2.0981 (machine direction (MD) 1% secant modulus)+564.28; where the AHTW is measured at a film thickness of about 2 mil, and the machine direction (MD) 1% secant modulus is measured at a film thickness of about 1 mil.

In an embodiment of the disclosure, film satisfies the following relationship: oxygen transmission rate (OTR)>−5.4297 (machine direction (MD) 1% secant modulus)+1767.8; where the OTR is measured at a film thickness of about 1 mil, and the machine direction (MD) 1% secant modulus is measured at a film thickness of about 1 mil.

In an embodiment of the disclosure, film satisfies the following relationship: seal initiation temperature (SIT)<0.366 (machine direction (MD) 1% secant modulus)+22.509; where the SIT is measured at a film thickness of about 2 mil, and the machine direction (MD) 1% secant modulus is measured at a film thickness of about 1 mil.

In an embodiment of the disclosure, film satisfies each of the following relationships: i) area of hot tack window (AHTW)>−2.0981 (machine direction (MD) 1% secant modulus)+564.28, where the AHTW is measured at a film thickness of about 2 mil, and the machine direction (MD) 1% secant modulus is measured at a film thickness of about 1 mil; ii) oxygen transmission rate (OTR)>−5.4297 (machine direction (MD) 1% secant modulus)+1767.8, where the OTR is measured at a film thickness of about 1 mil, and the machine direction (MD) 1% secant modulus is measured at a film thickness of about 1 mil; and iii) seal initiation temperature (SIT)<0.366 (machine direction (MD) 1% secant modulus)+22.509, where the SIT is measured at a film thickness of about 2 mil, and the machine direction (MD) 1% secant modulus is measured at a film thickness of about 1 mil.

In an embodiment of the disclosure, a film layer having a thickness of from 0.5 to 10 mil, satisfies at least one of the following relationships: i) area of hot tack window (AHTW) −2.0981 (machine direction (MD) 1% secant modulus)+564.28, where the AHTW is measured at a film thickness of about 2 mil, and the machine direction (MD) 1% secant modulus is measured at a film thickness of about 1 mil; ii) oxygen transmission rate (OTR)>−5.4297 (machine direction (MD) 1% secant modulus)+1767.8, where the OTR is measured at a film thickness of about 1 mil, and the machine direction (MD) 1% secant modulus is measured at a film thickness of about 1 mil; and iii) seal initiation temperature (SIT)<0.366 (machine direction (MD) 1% secant modulus)+22.509, where the SIT is measured at a film thickness of about 2 mil, and the machine direction (MD) 1% secant modulus is measured at a film thickness of about 1 mil.

In an embodiment of the disclosure, a film layer having a thickness of from 0.5 to 10 mil, satisfies each of the following relationships: i) area of hot tack window (AHTW)>−2.0981 (machine direction (MD) 1% secant modulus)+564.28, where the AHTW is measured at a film thickness of about 2 mil, and the machine direction (MD) 1% secant modulus is measured at a film thickness of about 1 mil; ii) oxygen transmission rate (OTR)>−5.4297 (machine direction (MD) 1% secant modulus)+1767.8, where the OTR is measured at a film thickness of about 1 mil, and the machine direction (MD) 1% secant modulus is measured at a film thickness of about 1 mil; and iii) seal initiation temperature (SIT)<0.366 (machine direction (MD) 1% secant modulus)+22.509, where the SIT is measured at a film thickness of about 2 mil, and the machine direction (MD) 1% secant modulus is measured at a film thickness of about 1 mil.

The films used in the manufactured articles described in this section may optionally include, depending on its intended use, additives and adjuvants. Non-limiting examples of additives and adjuvants include, anti-blocking agents, antioxidants, heat stabilizers, slip agents, processing aids, anti-static additives, colorants, dyes, filler materials, light stabilizers, light absorbers, lubricants, pigments, plasticizers, nucleating agents and combinations thereof.

The following examples are presented for the purpose of illustrating selected embodiments of this disclosure; it being understood, that the examples presented do not limit the claims presented.

EXAMPLES

Test Methods

Prior to testing, each specimen was conditioned for at least 24 hours at 23±2° C. and 50±10% relative humidity and subsequent testing was conducted at 23±2° C. and 50±10% relative humidity. Herein, the term “ASTM conditions” refers to a laboratory that is maintained at 23±+2C and 50±10% relative humidity; and specimens to be tested were conditioned for at least 24 hours in this laboratory prior to testing. ASTM refers to the American Society for Testing and Materials.

Density was determined using ASTM D792-13 (Nov. 1, 2013).

Melt index was determined using ASTM D1238 (Aug. 1, 2013). Melt indexes, I₂, I₆, I₁₀ and I₂₁ were measured at 190° C., using weights of 2.16 kg, 6.48 kg, 10 kg and a 21.6 kg respectively. Herein, the term “stress exponent” or its acronym “S.Ex.”, is defined by the following relationship: S.Ex.=log (I₆/I₂)/log(6480/2160); wherein I₆ and I₂ are the melt flow rates measured at 190° C. using 6.48 kg and 2.16 kg loads, respectively.

M_(n), M_(w), and M_(z) (g/mol) were determined by high temperature Gel Permeation Chromatography (GPC) with differential refractive index (DRI) detection using universal calibration (e.g. ASTM-D6474-99). GPC data was obtained using an instrument sold under the trade name “Waters 150c”, with 1,2,4-trichlorobenzene as the mobile phase at 140° C. The samples were prepared by dissolving the polymer in this solvent and were run without filtration. Molecular weights are expressed as polyethylene equivalents with a relative standard deviation of 2.9% for the number average molecular weight (“Mn”) and 5.0% for the weight average molecular weight (“Mw”). The molecular weight distribution (MWD) is the weight average molecular weight divided by the number average molecular weight, M_(W)/M_(n). The z-average molecular weight distribution is M_(z)/M_(n). Polymer sample solutions (1 to 2 mg/mL) were prepared by heating the polymer in 1,2,4-trichlorobenzene (TCB) and rotating on a wheel for 4 hours at 150° C. in an oven. The antioxidant 2,6-di-tert-butyl-4-methylphenol (BHT) was added to the mixture in order to stabilize the polymer against oxidative degradation. The BHT concentration was 250 ppm. Sample solutions were chromatographed at 140° C. on a PL 220 high-temperature chromatography unit equipped with four Shodex columns (HT803, HT804, HT805 and HT806) using TCB as the mobile phase with a flow rate of 1.0 mL/minute, with a differential refractive index (DRI) as the concentration detector. BHT was added to the mobile phase at a concentration of 250 ppm to protect the columns from oxidative degradation. The sample injection volume was 200 mL. The raw data were processed with Cirrus GPC software. The columns were calibrated with narrow distribution polystyrene standards. The polystyrene molecular weights were converted to polyethylene molecular weights using the Mark-Houwink equation, as described in the ASTM standard test method D6474.

The short chain branch frequency (e.g. the short chain branching per thousand backbone carbon atoms, or the SCB/1000C) of ethylene copolymer samples was determined by Fourier Transform Infrared Spectroscopy (FTIR) as per the ASTM D6645-01 method. A Thermo-Nicolet 750 Magna-IR Spectrophotometer equipped with OMNIC version 7.2a software was used for the measurements. Unsaturations in the polyethylene composition were also determined by Fourier Transform Infrared Spectroscopy (FTIR) as per ASTM D3124-98.

High temperature GPC equipped with an online FTIR detector (GPC-FTIR) was used to measure the comonomer content as the function of molecular weight.

Crystallization Elution Fractionation (CEF): A polymer sample (20 to 25 mg) was weighed into the sample vial and loaded onto the auto-sampler of the Polymer CEF unit. The vail was filled with 6 to 7 ml 1,2,4-trichlorobenzene (TCB), heated to the desired dissolution temperature (e.g. 160° C.) with a shaking rate of level number 3 for 2 hours. The solution (0.5 ml) was then loaded into the CEF columns (two CEF columns purchased from Polymer Char and installed in series). After allowed to equilibrate at a given stabilization temperature (e.g. 115° C.) for 5 minutes, the polymer solution was allowed to crystallize with a temperature drop from the stabilization temperature to 30° C. After equilibrating at 30° C. for 10 minutes, the soluble fraction was eluted at 30° C. for 10 minutes, followed by the crystallized sample eluted with TCB with a temperature ramp from 30° C. to 110° C. The CEF columns were cleaned at the end of the run for 5 minutes at 150° C. The other CEF run conditions were as follows: cooling rate 0.5° C./minute, flow rate in crystallization 0.02 mL/minute, heating rate 1.0° C./minute and flow rate in elution 2.0 mL/minute. The data were processed using Excel spreadsheet. The “CDBI₅₀” is defined as the weight percent of ethylene polymer whose composition is within 50% of the median comonomer composition (50% on each side of the median comonomer composition). The “CDBI₅₀” may be calculated from the composition distribution curve, determined by the CEF procedure described above, and the normalized cumulative integral of the composition distribution curve, as illustrated in U.S. Pat. No. 5,376,439 or WO 93/03093.

The “Composition Distribution Branching Index” or “CDBI” may alternatively by determined using a crystal-TREF unit commercially available form Polymer ChAR (Valencia, Spain). The acronym “TREF” refers to Temperature Rising Elution Fractionation. A sample of the polyethylene composition (80 to 100 mg) was placed in the reactor of the Polymer ChAR crystal-TREF unit, the reactor was filled with 35 ml of 1,2,4-trichlorobenzene (TCB), heated to 150° C. and held at this temperature for 2 hours to dissolve the sample. An aliquot of the TCB solution (1.5 mL) was then loaded into the Polymer ChAR TREF column filled with stainless steel beads and the column was equilibrated for 45 minutes at 110° C. The polyethylene composition was then crystallized from the TCB solution, in the TREF column, by slowly cooling the column from 110° C. to 30° C. using a cooling rate of 0.09° C. per minute. The TREF column was then equilibrated at 30° C. for 30 minutes. The crystallized polyethylene composition was then eluted from the TREF column by passing pure TCB solvent through the column at a flow rate of 0.75 mL/minute as the temperature of the column was slowly increased from 30° C. to 120° C. using a heating rate of 0.25° C. per minute. Using Polymer ChAR software a TREF distribution curve was generated as the polyethylene composition was eluted from the TREF column, i.e. a TREF distribution curve is a plot of the quantity (or intensity) of polyethylene composition eluting from the column as a function of TREF elution temperature. A CDBI₅₀ may be calculated from the TREF distribution curve for each polyethylene composition analyzed. The “CDBI₅₀” is defined as the weight percent of ethylene polymer whose composition is within 50% of the median comonomer composition (50% on each side of the median comonomer composition); it is calculated from the TREF composition distribution curve and the normalized cumulative integral of the TREF composition distribution curve. Those skilled in the art will understand that a calibration curve is required to convert a TREF elution temperature to comonomer content, i.e. the amount of comonomer in the polyethylene composition fraction that elutes at a specific temperature. The generation of such calibration curves are described in references such as, e.g. Wild, et al., J. Polym. Sci., Part B, Polym. Phys., Vol. 20 (3), pages 441-455: hereby fully incorporated by reference. Note: The “CDBI₂₅” is defined as the weight percent of polyethylene composition whose composition is within 25% of the median comonomer composition (25% on each side of the median comonomer composition).

Dynamic mechanical analyses were carried out with a rheometer, namely Rheometrics Dynamic Spectrometer (RDS-II) or Rheometrics SR5 or ATS Stresstech, on compression molded samples under nitrogen atmosphere at 190° C., using 25 mm diameter cone and plate geometry. The oscillatory shear experiments were done within the linear viscoelastic range of strain (10% strain) at frequencies from 0.05 to 100 rad/s. The values of storage modulus (G′), loss modulus (G″), complex modulus (G*) and complex viscosity (η*) were obtained as a function of frequency. The same rheological data can also be obtained by using a 25 mm diameter parallel plate geometry at 190° C. under nitrogen atmosphere. The Zero shear viscosity is estimated using the Ellis model, i.e. η(ω)=η₀/(1+τ/τ_(1/2) ^(α-1), where η₀ is the zero shear viscosity. τ_(1/2) is the value of the shear stress at which η=η₀/2 and a is one of the adjustable parameters. The Cox-Merz rule is assumed to be applicable in the present disclosure.

The DRI, is the “dow rheology index”, and is defined by the equation: DRI=[365000(τ₀/η₀)−1]/10; wherein τ₀ is the characteristic relaxation time of the polyethylene and η₀ is the zero shear viscosity of the material. The DRI is calculated by least squares fit of the rheological curve (dynamic complex viscosity versus applied frequency e.g. 0.01-100 rads/s) as described in U.S. Pat. No. 6,114,486 with the following generalized Cross equation, i.e. η(ω)=η₀/[1+(ωτ₀)^(n)]; wherein n is the power law index of the material, η(ω) and ω are the measured complex viscosity and applied frequency data respectively. When determining the DRI, the zero shear viscosity, η₀ used was estimated with the Ellis model, rather than the Cross model.

The crossover frequency is the frequency at which storage modulus (G′) and loss modulus (G″) curves cross with each other, while G′@G″=500 Pa is the storage modulus at which the loss modulus (G″) is at 500 Pa.

Primary melting peak (° C.), melting peak temperatures (° C.), heat of fusion (J/g) and crystallinity (%) was determined using differential scanning calorimetry (DSC) as follows: the instrument was first calibrated with indium; after the calibration, a polymer specimen is equilibrated at 0° C. and then the temperature was increased to 200° C. at a heating rate of 10° C./min; the melt was then kept isothermally at 200° C. for five minutes; the melt was then cooled to 0° C. at a cooling rate of 10° C./min and kept at 0° C. for five minutes; the specimen was then heated to 200° C. at a heating rate of 10° C./min. The DSC Tm, heat of fusion and crystallinity are reported from the 2^(nd) heating cycle.

Film dart impact strength was determined using ASTM D1709-09 Method A (May 1, 2009). In this disclosure the dart impact test employed a 1.5 inch (38 mm) diameter hemispherical headed dart.

The film “ASTM puncture” is the energy (J/mm) required to break the film was determined using ASTM D5748-95 (originally adopted in 1995, reapproved in 2012). The puncture test is performed on a mechanical tester, in which the puncture probe is attached to the load cell which is mounted on a moving crosshead. The film is clamped into a clamping mechanism which has a 4 inch (102 mm) diameter opening. The clamping mechanism is attached to a fixed plate. The cross head speed is set at 10 in/min (255 mm/min). The maximum force and energy to puncture the film are recorded.

The “slow puncture” or “lubricated puncture” test was performed as follows: the energy (J/mm) to puncture a film sample was determined using a 0.75-inch (1.9-cm) diameter pear-shaped fluorocarbon coated probe travelling at 10-inch per minute (25.4-cm/minute). ASTM conditions were employed. Prior to testing the specimens, the probe head was manually lubricated with Muko Lubricating Jelly to reduce friction. Muko Lubricating Jelly is a water-soluble personal lubricant available from Cardinal Health Inc., 1000 Tesma Way, Vaughan, ON L4K 5R₈ Canada. The probe was mounted in an Instron Model 5 SL Universal Testing Machine and a 1000-N load cell as used. Film samples (1.0 mil (25 μm) thick, 5.5 inch (14 cm) wide and 6 inch (15 cm) long) were mounted in the Instron and punctured. The following film tensile properties were determined using ASTM D882-12 (Aug. 1, 2012): tensile break strength (MPa), elongation at break (%), tensile yield strength (MPa), tensile elongation at yield (%) and film toughness or total energy to break (ft·lb/in³). Tensile properties were measured in the both the machine direction (MD) and the transverse direction (TD) of the blown films.

The secant modulus is a measure of film stiffness. The secant modulus is the slope of a line drawn between two points on the stress-strain curve, i.e. the secant line. The first point on the stress-strain curve is the origin, i.e. the point that corresponds to the origin (the point of zero percent strain and zero stress), and; the second point on the stress-strain curve is the point that corresponds to a strain of 1%; given these two points the 1% secant modulus is calculated and is expressed in terms of force per unit area (MPa). The 2% secant modulus is calculated similarly. This method is used to calculated film modulus because the stress-strain relationship of polyethylene does not follow Hook's law; i.e. the stress-strain behavior of polyethylene is non-linear due to its viscoelastic nature. Secant moduli were measured using a conventional Instron tensile tester equipped with a 200 lbf load cell. Strips of monolayer film samples were cut for testing with following dimensions: 14 inch long, 1 inch wide and 1 mil thick; ensuring that there were no nicks or cuts on the edges of the samples. Film samples were cut in both the machine direction (MD) and the transverse direction (TD) and tested. ASTM conditions were used to condition the samples. The thickness of each film was accurately measured with a hand-held micrometer and entered along with the sample name into the Instron software. Samples were loaded in the Instron with a grip separation of 10 inch and pulled at a rate of 1 inch/min generating the strain-strain curve. The 1% and 2% secant modulus were calculated using the Instron software.

The oxygen transmission rate (OTR) of the blown film was tested using an Oxtran 2/20 instrument manufactured by MOCON Inc, Minneapolis, Minn., USA. The instrument has two test cells (A and B) and each film sample was analyzed in duplicate. The OTR result reported is the average of the results from these two test cells (A and B). The test is carried out at a temperature of 23° C. and at a relative humidity of 0%. The film sample area used for testing was 100 cm². The carrier gas used was 2% hydrogen gas in a balance of nitrogen gas and the test gas is ultra high purity oxygen. The blown films which were tested each had a film thickness of 1 mil.

Puncture-propagation tear resistance of blown film was determined using ASTM D2582-09 (May 1, 2009). This test measures the resistance of a blown film to snagging, or more precisely, to dynamic puncture and propagation of that puncture resulting in a tear. Puncture-propagation tear resistance was measured in the machine direction (MD) and the transverse direction (TD) of the blown films.

Film tear performance was determined by ASTM D1922-09 (May 1, 2009); an equivalent term for tear is “Elmendorf tear”. Film tear was measured in both the machine direction (MD) and the transverse direction (TD) of the blown films.

Film optical properties were measured as follows: Haze, ASTM D1003-13 (Nov. 15, 2013), and; Gloss ASTM D2457-13 (Apr. 1, 2013).

In this disclosure, the “Hot Tack Test” was performed as follows, using ASTM conditions. Hot tack data was generated using a J&B Hot Tack Tester which is commercially available from Jbi Hot Tack, Geloeslaan 30, B-3630 Maamechelen, Belgium. In the hot tack test, the strength of a polyolefin to polyolefin seal is measured immediately after heat sealing two film samples together (the two film samples were cut from the same roll of 2.0 mil (51-μm) thick film), i.e. when the polyolefin macromolecules that comprise the film are in a semi-molten state. This test simulates the heat sealing of polyethylene films on high speed automatic packaging machines, e.g., vertical or horizontal form, fill and seal equipment. The following parameters were used in the J&B Hot Tack Test: film specimen width, 1 inch (25.4 mm); film sealing time, 0.5 second; film sealing pressure, 0.27 N/mm²; delay time, 0.5 second; film peel speed, 7.9 in/second (200 mm/second); testing temperature range, 131° F. to 293° F. (55° C. to 145° C.); temperature increments, 9° F. (5° C.); and five film samples were tested at each temperature increment to calculate average values at each temperature. In this way, a hot tack profile of pulling force vs sealing temperature is generated. The following data can be calculated from this hot tack profile: the “Tack Onset @ 1.0 N (° C.)”, is the temperature at which a hot tack force of 1N was observed (an average of five film samples); the “Max Hot tack Strength (N)”, is the maximum hot tack force observed (an average of five film samples) over the testing temperature range; the “Temperature—Max. Hot tack (° C.)”, is the temperature at which the maximum hot tack force was observed. Finally, the area of the hot-tack (strength) window (the “area of hot tack window” or the “AHTW”) is an estimate of the area under this hot tack profile from the hot-tack on-set temperature to the temperature immediately prior to the melting of the specimen. The latter temperature prior to the melting of the specimen is typically at 130° C., but not necessarily at 130° C. Piece-wise regressions (linear or polynomial) were performed for different segments of the hot tack profile to obtain the mathematical relationships between seal temperature and pulling force. The partial area of each temperature-force segment was then calculated. The total area (AHTW) is the summation of each partial area of each segment of the hot tack profile within the specified range (i.e., from the hot-tack on-set temperature to the temperature immediately prior to the melting of the specimen).

In this disclosure, the “Heat Seal Strength Test” (also known as “the cold seal test”) was performed as follows. ASTM conditions were employed. Heat seal data was generated using a conventional Instron Tensile Tester. In this test, two film samples are sealed over a range of temperatures (the two film samples were cut from the same roll of 2.0 mil (51-μm) thick film). The following parameters were used in the Heat Seal Strength (or cold seal) Test: film specimen width, 1 inch (25.4 mm); film sealing time, 0.5 second; film sealing pressure, 40 psi (0.28 N/mm²); temperature range, 212° F. to 302° F. (100° C. to 150° C.) and temperature increment, 9° F. (5° C.). After aging for at least 24 hours at ASTM conditions, seal strength was determined using the following tensile parameters: pull (crosshead) speed, 12 inch/min (2.54 cm/min); direction of pull, 90° to seal, and; 5 samples of film were tested at each temperature increment. The Seal Initiation Temperature, hereafter S.I.T., is defined as the temperature required to form a commercially viable seal; a commercially viable seal has a seal strength of 2.0 lb. per inch of seal (8.8 N per 25.4 mm of seal).

The hexane extractable content of a polymer sample was determined according to the Code of Federal Registration 21 CFR § 177.1520 Para (c) 3.1 and 3.2; wherein the quantity of hexane extractable material in a film is determined gravimetrically. Elaborating, 2.5 grams of 3.5 mil (89 μm) monolayer film was placed in a stainless steel basket, the film and basket were weighed (w^(i)), while in the basket the film was: extracted with n-hexane at 49.5° C. for two hours; dried at 80° C. in a vacuum oven for 2 hours; cooled in a desiccator for 30 minutes, and; weighed (w^(f)). The percent loss in weight is the percent hexane extractable (w^(C6)): w^(C6)=100×(w^(i)−w^(f))/w^(l).

Polyethylene Compositions

A polyethylene composition comprising a first, second and third polyethylene was made by melt blending polyethylene composition A with polyethylene B.

Polyethylene composition A was made using two different single site catalysts in a dual parallel reactor solution polymerization process. As a result, polyethylene composition A comprised a first polyethylene made with first single site catalyst (a metallocene) and a second polyethylene made with a second single site catalyst (a phosphinimine catalyst). A parallel mode solution phase polymerization reactor process has been described in U.S. patent application Ser. No. 15/491,264 (co-pending with the present application). Basically, in parallel mode the exit streams exiting each of a first reactor (R1) and a second reactor (R2) are combined downstream of each reactor and the polymer product is obtained after devolatilization.

The following examples illustrate the continuous solution copolymerization of ethylene and 1-octene at medium pressure in a dual reactor system connected in parallel. The first and second reactor pressure was about 16,000 kPa (about 2.3×10³ psi). The first reactor was operated at a lower temperature than the second reactor. The first reactor had a volume of 12 liters and the second reactor had a volume of 24 liters. Both reactors were agitated to ensure good mixing of the reactor contents. The process was continuous in all feed streams (i.e. solvents, which were methyl pentane and xylene; monomers and catalyst and cocatalyst components) and in the removal of product. Monomer (ethylene) and comonomer (1-octene) were purified prior to addition to the reactor using conventional feed preparation systems (such as contact with various absorption media to remove impurities such as water, oxygen and polar contaminants). The reactor feeds were pumped to the reactors at the ratios shown in Table 1. Average residence times for the reactors are calculated by dividing average flow rates by reactor volume. The residence time in each reactor for all of the inventive experiments was less than 10 minutes and the reactors were well mixed. The catalyst deactivator used was octanoic acid (caprylic acid), commercially available from P&G Chemicals, Cincinnati, Ohio, U.S.A.

The following single site catalyst (SSC) components were used to prepare the first polyethylene in a first reactor (R1) configured in parallel to a second reactor (R2): diphenylmethylene(cyclopentadienyl)(2,7-di-t-butylfuorenyl)hafnium dimethide [(2,7-tBu₂Flu)Ph₂C(Cp)HfMe₂]; methylaluminoxane (MMAO-07); trityl tetrakis(pentafluoro-phenyl)borate (trityl borate), and 2,6-di-tert-butyl-4-ethylphenol (BHEB). Methylaluminoxane (MMAO-07) and 2,6-di-tert-butyl-4-ethylphenol are premixed in-line and then combined with diphenylmethylene(cyclopentadienyl)(2,7-di-t-butylfuorenyl)hafnium dimethide and trityl tetrakis(pentafluoro-phenyl)borate just before entering the polymerization reactor (R1).

The following single site catalyst (SSC) components were used to prepare the first polyethylene in a second reactor (R2) configured in parallel to a first reactor (R1): cyclopentadienyl tri(tertiary butyl)phosphinimine titanium dichloride [Cp((t-Bu)₃PN)TiCl₂]; methylaluminoxane (MMAO-07); trityl tetrakis(pentafluoro-phenyl)borate (trityl borate), and 2,6-di-tert-butyl-4-ethylphenol (BHEB). Methylaluminoxane (MMAO-07) and 2,6-di-tert-butyl-4-ethylphenol are premixed in-line and then combined with cyclopentadienyl tri(tertiarybutyl)phosphinimine titanium dichloride [Cp((t-Bu)₃PN)TiCl₂] and trityl tetrakis(pentafluoro-phenyl)borate just before entering the polymerization reactor (R2).

Polyethylene C, on the other hand is made in a single solution polymerization reactor using a Ziegler-Natta catalyst as described below; however, in this example the in-line formed Ziegler-Natta catalyst was fed only to a first reactor (R1) to prepare polyethylene C in a single reactor. For the sake of clarity, polyethylene C becomes the third polyethylene within the final polyethylene composition. The following Ziegler-Natta (ZN) catalyst components were used to prepare the third polyethylene: butyl ethyl magnesium; tertiary butyl chloride; titanium tetrachloride; diethyl aluminum ethoxide; and triethyl aluminum. Methylpentane was used as the catalyst component solvent and the in-line Ziegler-Natta catalyst formulation was prepared using the following steps. In step one, a solution of triethylaluminum and butyl ethyl magnesium (Mg:Al=20, mol:mol) was combined with a solution of tertiary butyl chloride and allowed to react for about 30 seconds to produce a MgCl₂ support. In step two, a solution of titanium tetrachloride was added to the mixture formed in step one and allowed to react for about 14 seconds prior to injection into reactor (R1). The in-line Ziegler-Natta catalyst was activated in the reactor by injecting a solution of diethyl aluminum ethoxide into R1. The quantity of titanium tetrachloride added to the reactor is shown in Table 1. The efficiency of the in-line Ziegler-Natta catalyst formulation was optimized by adjusting the mole ratios of the catalyst components.

Table 1, shows the reactor conditions used to make polyethylene composition A, as well as polyethylene B. The properties of polyethylene composition A, as well as polyethylene B are shown in Table 2.

TABLE 1 Reactor Operating Conditions Blending Component PE Composition A SSC in R1 and SSC PE B in R2 (dual reactor ZN in R1 (single Description in parallel mode) reactor) Reactor 1 (R1) metallocene ZN TSR (kg/hr) 300 375 Ethylene concentration 7.9 9.3 (wt %) 1-Octene/ethylene in 0.82 0.65 fresh feed (g/g) Primary feed 35.0 35.0 temperature (° C.) Mean Temperature (° C.) 130.2 150.8 Ethylene conversion 80.1 91.3 Hydrogen Feed (ppm) 0.49 3.75 Catalyst (ppm) to R1 0.84 4.7 SSC - Al/Hf (mol/mol) 31 N/A SSC - BHEB/Al 0.4 N/A (mol/mol) SSC - B/Hf (mol/mol) 1.22 N/A ZN - N/A 2.1 tertbutylchloride/Mg (mol/mol) ZN - Mg/Ti (mol/mol) N/A 7.0 ZN - diethyl aluminum N/A 1.35 ethoxide/Ti (mol/mol) Reactor 2 (R2) phosphinimine TSR (kg/hr) 300 N/A Ethylene concentration 13.4 N/A (wt %) 1-Octene/ethylene in 0.0 N/A fresh feed (g/g) Primary feed 35.3 N/A temperature (° C.) Mean Temperature (° C.) 190.9 N/A Ethylene conversion 90.0 N/A Hydrogen Feed (ppm) 5.31 N/A Catalyst (ppm) to R2 0.24 N/A SSC - Al/Ti (mol/mol) 65 N/A SSC - BHEB/Al 0.3 N/A (mol/mol) SSC - B/Ti (mol/mol) 1.5 N/A

TABLE 2 Blend Component Properties Blending Component PE Composition A SSC in R1 and SSC in R2 (dual PE B reactor in parallel ZN in R1 Description mode) (single reactor) Catalysts SSC/SSC ZN PS Sample No./ PS-125595 PS-125534 NOVA Lot No. Density (g/cm³) 0.9152 0.9164 Melt Index I₂ (g/10 min) 1.49 0.33 Melt Index I₆ (g/10 min) 6.95 1.36 Melt Index I₁₀ (g/10 min) 13.4 2.46 Melt Index I₂₁ (g/10 min) 52.2 8.74 Melt Flow Ratio 35 26.50 (I₂₁/I₂) Stress Exponent 1.40 1.28 Melt Flow Ratio 9.12 7.70 (I₁₀/I₂) Branch Frequency - FTIR Branch Freq/1000 C. 21.5 15.7 Comonomer 1-octene 1-octene Comonomer 4.30 3.10 Content (mole %) Comonomer 15.2 11.5 Content (weight %) Internal 0.013 0.005 Unsat/100 C. Side Chain 0.002 0.002 Unsat/100 C. Terminal 0.006 0.025 Unsat/100 C. GPC - Conventional M_(n) 49016 34317 M_(w) 105906 135987 M_(z) 215295 338832 Polydispersity 2.16 3.96 Index (M_(w)/M_(n))

The properties of two different polyethylene compositions which were obtained from melt blending polyethylene composition A with polyethylene B at two different weight fractions is provided in Table 3 as Inventive Examples 1 and 2. The materials were melt blended using a Coperion ZSK 26 co-rotating twin screw extruder with an L/D of 32:1. The extruder was fitted with an underwater pelletizer and a Gala spin dryer. The materials were co-fed to the extruder using gravimetric feeders to achieve the desired ratios of polyethylene composition A to polyethylene B. The blends were compounded using a screw speed of 200 rpm at an output rate of 15-20 kg/hour and at a melt temperature of 225-230° C.

Data for comparative polyethylene compositions, Comparative Examples 1-9 is also included in Table 3. Comparative Example 1 is ELITE® 5400G, a resin commercially available from the Dow Chemical Company. ELITE 5400G has a density of about 0.916 g/cm³ and a melt index I₂ of about 1 dg/min. Comparative Example 2 is SURPASS® FP117-C, a resin commercially available from the NOVA Chemicals Corporation. SURPASS FP117-C has a density of 0.917 g/cm³ and a melt index I₂ of 1 dg/min. Comparative Examples 3 and 4 are resins made according to U.S. Pat. Appl. Pub. No. 2016/0108221. Comparative Example 3 is an ethylene/1-octene copolymer, has a density of about 0.917 g/cm³, a melt index I₂ of about 0.96 dg/min, and is made in a multi reactor solution process in which a first reactor and a second reactor are configured in series with one another. Comparative Example 4 is an ethylene/1-octene copolymer, has a density of about 0.913 g/cm³, a melt index I₂ of about 0.85 dg/min, and is made in a multi reactor solution process in which a first reactor and a second reactor are configured in series with one another. Comparative Example 5 is SCLAIR® FP112-A, a resin commercially available from the NOVA Chemicals Corporation. SCLAIR FP112-A has a density of 0.912 g/cm³ and a melt index I₂ of 0.9 dg/min. Comparative Example 6 is EXCEED®1018CA, a resin commercially available from ExxonMobil. EXCEED 1018CA has a density of about 0.918 g/cm³ and a melt index I₂ of about 0.94 dg/min. Comparative Example 7 is MARLEX® D139, a resin commercially available from ChevronPhillips. MARLEX D139 has a density of about 0.918 g/cm³ and a melt index I₂ of about 0.9 dg/min. Comparative Example 8 is SCLAIR® FP120-A, a resin commercially available the NOVA Chemicals Corporation. FP120-A has a density of 0.920 g/cm³ and a melt index I₂ of 1 dg/min. Comparative Example 9 is SCLAIR® FP026-F, a resin commercially available the NOVA Chemicals Corporation. FP026-F has a density of 0.926 g/cm³ and a melt index I₂ of 0.75 dg/min.

TABLE 3 Polyethylene Composition Properties Example No. Invention 1 Inv. 2 (70 wt % PE (40 wt % PE Composition A/ Composition A/ 30 wt % PE B) 60 wt % PE B) Comp. 1 Comp. 2 Comp. 3 Comp. 4 Density (g/cm³) 0.9159 0.9162 0.9159 0.9166 0.9167 0.913 Melt Index I₂ 0.73 0.48 1 0.99 0.96 0.85 (g/10 min) Melt Index I₆ 3.48 2.14 4.46 4 3.72 3.09 (g/10 min) Melt Index I₁₀ 6.68 4.02 8.57 7.57 6.65 (g/10 min) Melt Index I₂₁ 26.4 15.5 31.3 29 24.4 (g/10 min) Melt Flow 36.3 32.5 31.4 29.4 25.4 21.5 Ratio (I₂₁/I₂) Stress 1.42 1.36 1.36 1.27 1.23 1.21 Exponent Melt Flow 9.52 8.72 8.61 7.67 7.24 6.78 Ratio (I₁₀/I₂) Rheological Properties Zero Shear 19940 23400 15600 8688 9433 11350 Viscosity - 190° C. (Pa-s) Crossover 80.53 50.76 110.98 73.56 81.27 98.88 Frequency - 190° C. (rad/s) DRI 1.78 0.78 2.41 0.26 0.23 0.22 G′@G″500 Pa = 133.18 82.92 79.3 22.8 23.9 32 Branch Frequency - FTIR Branch 19.7 17.7 15.2 14.1 15.6 17.1 Freq/1000 C Comonomer 1-octene 1-octene 1-octene 1-octene 1-octene 1-octene Comonomer 3.9 3.5 3 2.8 3.1 3.4 Content (mole %) Comonomer 14.1 12.8 11.2 10.4 11.4 12.7 Content (wt %) Internal 0.009 0.007 0.003 0.019 0.009 0.007 Unsat/100 C Side Chain 0.006 0.005 0.004 0.003 0.006 0.003 Unsat/100 C Terminal 0.012 0.02 0.029 0.006 0.046 0.027 Unsat/100 C CEF Soluble 30.33 19.4 2.05 0.77 3.78 2.42 fraction (%), ≤30° C. DSC First Melting 128.100 113.600 101 109 105.7 100.0 Peak (° C.) Second 126 118 112 117.4 119.3 Melting Peak (° C.) Third Melting — 122 — 121.2 122.8 Peak (° C.) Heat of Fusion 127 126.3 119 123 123.9 112.6 (J/g) Crystallinity 43.8 43.6 41.19 42.29 42.72 38.82 (%) GPC - Conventional M_(n) 45974 46076 36781 33939 33939 44573 M_(w) 119291 123764 99802 102503 102503 114666 M_(z) 277605 284944 210866 234321 234321 262824 Polydispersity 2.59 2.69 2.71 3.02 3.02 2.57 Index (M_(w)/M_(n)) Mz/Mw 2.33 2.30 2.11 2.29 2.29 2.29 Hexane 3.17 0.87 0.54 0.56 0.77 0.61 Extractables (%) - Plaque Example No. Comp. 5 Comp. 6 Comp. 7 Comp. 8 Comp. 9 Density (g/cm³) 0.912 0.919 0.918 0.920 0.926 Melt Index I₂ 0.9 0.94 0.89 1 0.75 (g/10 min) Melt Index I₆ 3.16 3.14 4.29 3.02 (g/10 min) Melt Index I₁₀ 5.16 5.22 — — (g/10 min) Melt Index I₂₁ 14.8 15.2 29.8 20.1 (g/10 min) Melt Flow 31.4 15.8 17.2 29.8 27 Ratio (I₂₁/I₂) Stress 1.34 1.11 1.15 1.32 1.31 Exponent Melt Flow 5.64 5.94 — — Ratio (I₀/I₂) Rheological Properties Zero Shear 12990 7731 9198 10783 14750 Viscosity - 190° C. (Pa-s) Crossover 83.76 159.80 149.38 107.5 91.93 Frequency - 190° C. (rad/s) DRI 0.01 0.09 — — G′@G″500 Pa = 45.7 8 34.1 41.9 47.7 Branch Frequency - FTIR Branch 19.2 13.4 13.1 Freq/1000 C Comonomer 1-octene 1-hexene 1-hexene 1-octene 1-octene Comonomer 3.8 2.7 2.6 2.6 1.7 Content (mole %) Comonomer 13.8 9.9 9.7 9.7 6.3 Content (wt %) Internal 0.007 0.002 0.006 0.005 0.002 Unsat/100 C Side Chain 0.007 0.004 0.005 0.006 0.004 Unsat/100 C Terminal 0.045 0.01 0.007 0.052 0.048 Unsat/100 C CEF Soluble 7.13 0.57 0.57 2.85 1.14 fraction (%), ≤30° C. DSC First Melting 102.0 109.52 106.26 108.93 115.24 Peak (° C.) Second 117.9 118.08 116.62 119.52 121.5 Melting Peak (° C.) Third Melting 121.6 — — — Peak (° C.) Heat of Fusion 110.6 126.96 125.56 132.95 144.24 (J/g) Crystallinity 38.14 43.78 43.29 45.84 49.74 (%) GPC - Conventional M_(n) 33139 55850 55399 31575 35549 M_(w) 118358 110641 106175 101954 112255 M_(z) 379353 186289 180670 302775 297745 Polydispersity 3.57 1.98 1.92 3.40 3.16 Index (M_(w)/M_(n)) Mz/Mw 3.21 1.68 1.70 2.82 2.65 Hexane 1.40 0.26 0.37 0.44 0.22 Extractables (%) - Plaque

Details of the Inventive polyethylene composition components: the first polyethylene, the second polyethylene, and the third polyethylene, are provided in Table 4. With the exception of the weight percentages, w1 and w2 (which are found by adjusting the de-convoluted values, w1′ and w2′, as is further discussed below) the data in Table 4 includes the mathematically de-convoluted component properties of polyethylene composition A (which comprised the first polyethylene which was made with a single site metallocene catalyst and the second polyethylene which was made with a single site phosphinimine catalyst) as well as the experimentally determined properties of polyethylene B (the third polyethylene which was made with a Ziegler-Natta catalyst).

High temperature GPC equipped with an online FTIR detector (GPC-FTIR) was used to measure the comonomer content as a function of molecular weight. In order to de-convolute the polyethylene composition A (which results from use of a SSC in R1 and R2 in parallel mode polymerization) into components, the mathematical deconvolution model described in U.S. Pat. No. 8,022,143 was used. The mathematical deconvolution of the GPC and GPC-FTIR data, the molecular weight distribution of the first polyethylene (the SSC component made in R1, considered one catalyst site) and the second polyethylene (the SSC component made in R2, considered one catalyst site) was modeled using a single Schultz Flory distribution (where the Mw/Mn was assumed to be 2; the M_(n) was M_(w)/2 and the Mz was 1.5×Mw) as described in U.S. Pat. No. 8,022,143. To improve the deconvolution accuracy and consistency, as a constraint, the melt index, I₂, of the modeled composition (i.e. the dual-reactor polyethylene composition A) was set and the following relationship was satisfied during the deconvolution: Log₁₀(I ₂)=22.326528+0.003467*[Log₁₀(M _(n))]³−4.322582*Log₁₀(M _(w))-0.180061*[Log₁₀(Mz)]²+0.026478*[Log₁₀(Mz)]³ where the experimentally measured overall melt index (i.e. of polyethylene composition A), I₂, was used on the left side of the equation. Hence, a total of two sites (one for each SSC) were used to de-convolute polyethylene composition A. The w(i) and Mn(i), i=1 to 2, were obtained while Mw(i) and Mz(i) of each site were calculated using the above relationships using Mn(i) for each site. During the deconvolution, the overall M_(n), M_(w) and M_(z) of polyethylene composition A was calculated with the following relationships: M_(n)=1/Sum(w_(i)/M_(n)(i)), M_(w)=Sum(w_(i)×M_(w)(i)), M_(z)=Sum(w_(i)×M_(z)(i)²), where i represents the i-th component and w_(i) represents the relative weight fraction of the i-th component in the composition from the above 2-site deconvolution. The GPC-FTIR chromatograph profile was subsequently deconvoluted using the w(i) results to obtain SCB(i), i=1 to 2.

The Mn, Mw, Mz and SCB/1000C of the first and second polyethylenes made with a SSC in each of R1 and R2 were then calculated using the above relationships, with the above data of Mn(i), Mw (i), Mz(i), SCB(i) for each catalyst site.

When the polymer made with the single site catalyst in R2 was an ethylene homopolymer, as is the case in the present examples, then during the deconvolution analysis the SCB/1000C for the modeled SSC site was set as zero. If however, the polymer made by the SSC was a copolymer, then the SCB value would be determined for the SSC site using the deconvolution model presented above.

In order to calculate the melt index, I₂ of each of the first and second polyethylenes in polyethylene composition A, the following melt index, I₂ model was used: Log₁₀(melt index,I ₂)=22.326528+0.003467*[Log₁₀(M _(n))]³−4.322582*Log₁₀(M _(w))−0.180061*[Log₁₀(M _(z))]²+0.026478*[Log₁₀(M _(z))]³ where the M_(n), M_(w) and M_(z) were the deconvoluted values of the first or second polyethylene components present in polyethylene composition A, as obtained from the results of the above GPC deconvolution.

The density of the first polyethylene which was an ethylene copolymer made using a single site catalyst in R1 was calculated using the following density model: density of the first polyethylene made with a SSC=0.979863-0.00594808*(FTIR SCB/1000C)^(0.65)−0.000383133*[Log₁₀(M _(n))]³−0.00000577986*(M _(w) /M _(n))³+0.00557395*(M _(Z) /M _(w))^(0.25) where the M_(n), M_(w) and M_(z) were the deconvoluted values of the first polyethylene as obtained from the results of the above GPC deconvolution and the SCB/1000C was obtained from the GPC-FTIR deconvolution. The density of the second polyethylene which was an ethylene homopolymer made with a single site catalyst in R₂ was determined using the same equation used above for finding the density of the first polyethylene, but with the value for the short chain branching set to zero to cancel out the corresponding term: density of the second polyethylene made with a SSC=0.979863−0.000383133*[Log₁₀(M _(n))]³−0.00000577986*(M _(w) /M _(n))³+0.00557395*(M _(z) /M _(w))^(0.25).

The de-convolution provided the density (d1, and d2), melt index (I₂ ¹ and I₂ ²), short chain branching (SCB1 with the SCB2 being set as zero for an ethylene homopolymer) the weight average and number average molecular weights (Mw1, Mn1, Mw2 and Mn2), and the weight fraction (w1′ and w2′) of the first and second polyethylenes The resulting deconvoluted properties as well as the relative weight percentages w1, w2 (which for the first and the second polyethylenes, respectively, are found by modifying the deconvoluted weight fractions w1′ and w2′ to match the amount of polyethylene composition A in the final melt blended polyethylene composition, as determined by the blending rules discussed further below) are provided in Table 4.

The following basic blending rules were used to achieve the desired polyethylene compositions comprising a first, a second and a third polyethylene:

w1=weight percentage of the first polyethylene in the final polyethylene composition;

-   -   w2=weight percentage of the second polyethylene in the final         polyethylene composition;     -   w3=weight percentage of the third polyethylene in the final         polyethylene composition;     -   w1*=weight percentage of polyethylene composition A in the melt         blend; w2*=weight percentage of polyethylene B in the melt         blend;     -   w1′=weight percentage of the first polyethylene in polyethylene         composition A (i.e. the w1′ determined from the mathematical         deconvolution of polyethylene composition A);     -   w2′=weight percentage of the second polyethylene in polyethylene         composition A (i.e. the w2′ determined from the mathematical         deconvolution of polyethylene composition A);     -   where,         -   w1+w2+w3=1;         -   w1*+w2*=1; and         -   w1′+w2′=1;     -   so that,         -   w1=w1*×w1′;         -   w2=w1*×w2′; and         -   w3=w2*.

TABLE 4 Polyethylene Composition Component Properties Example No. Inventive PE Inventive PE Composition 1 Composition 2 Polyethylene Composition Density (g/cm³) 0.9159 0.9162 I₂ (dg/min) 0.73 0.48 Stress Exponent 1.42 1.36 MFR (I₂₁/I₂) 36.3 32.5 Mn 45974 46076 Mw 119291 123764 Mz 277605 284944 Mw/Mn 2.59 2.69 Mz/Mw 2.33 2.30 The First Polyethylene Catalyst Type 1 Single Site Catalyst Single Site Catalyst (metallocene) (metallocene) weight fraction, w1 0.308 0.176 (note: w1′ = 0.44 from (note: w1′ = 0.44 from deconvolution) deconvolution) Mn1 65750 65750 Mw1 131500 131500 Mw1/Mn1 2 (Mw1/Mn1 < 2.3) 2 (Mw1/Mn1 < 2.3) short chain branches per 49 49 1000 carbons I₂ ¹ (g/10 min.) 0.3 0.3 d1 (g/cm³) 0.8685 0.8685 The Second Polyethylene Catalyst Type 2 Single Site Catalyst Single Site Catalyst (phosphinimine) (phosphinimine) weight fraction, w2 0.392 0.224 (note: w2′ = 0.56 from (note: w2′ = 0.56 from deconvolution) deconvolution) Mn2 25450 25450 Mw2 50900 50900 Mw2/Mn2 2 (Mw2/Mn2 < 2.3) 2 (Mw2/Mn2 < 2.3) short chain branches per 0 0 1000 carbons I₂ ² (g/10 min) 11.67 11.67 d2 (g/cm³) 0.9532 0.9532 The Third Polyethylene Catalyst Type 3 Ziegler-Natta Catalyst Ziegler-Natta Catalyst weight fraction, w3 0.300 0.600 Mn3 34317 34317 Mw3 135987 135987 Mw3/Mn3 3.96 (Mw3/Mn3 > 2.3) 3.96 (Mw3/Mn3 > 2.3) short chain branches per 15.7 15.7 1000 carbons I₂ ³ (g/10 min) 0.33 0.33 d3 (g/cm³) 0.9164 0.9164

With reference to FIG. 1, a person skilled in the art will recognize that the inventive polyethylene compositions have a unimodal GPC profile.

With reference to FIG. 2, a person skilled in the art will recognize that the inventive polyethylene compositions have a partially reverse comonomer incorporation, where the comonomer incorporation first rises as molecular weight increases, and then falls as the molecular weight increases still further.

With reference to FIG. 3, a person skilled in the art will recognize that the inventive polyethylene compositions each have a melting peak which occurs at above 125° C. For Inventive Example 1 the DSC profile is unimodal. For Inventive Example 2, the DSC profile is bimodal.

The data in Table 3, clearly shows that in contrast to each of the comparative resins, the inventive polyethylene compositions have a significant amount of material eluting at lower temperature in a crystallization elution fractionation (CEF) analysis. Inventive Examples 1 and 2, each have a soluble fraction in a crystallization elution fractionation (CEF) analysis of greater than 10 weight percent (Inventive Example 1, is 30.3 weight percent; Inventive Example 2, is 19.4 weight percent), while all of the Comparative Examples 1-9, have a soluble fraction in a crystallization elution fractionation (CEF) analysis (i.e. a fraction eluting at or below 30° C.) of less than 10 weight percent.

Blown films were generated by using a 2.5-inch Gloucester blown film line (L/D=24) with a die diameter of 4-inch. The die was coated with polymer processing aid (PPA) by spiking the line with a high concentration of PPA masterbatch to avoid melt fracture. The fixed conditions were die gap of 35 mils (0.0889 cm), frost line height of about 17 inches and output of 100 lbs/hr. Films were collected under different orientation conditions. The monolayer 1-mil film was produced with a blow up ratio (BUR) of 2.5 and the 1-mil films were used for obtaining the physical properties of the films. The monolayer 2-mil film (BUR=2.5) was used for obtaining the cold-seal and hot tack profiles. Data for film blown from the polyethylene compositions of the present disclosure is provided in Table 5, along with data for films made from various comparative resins.

Comparative Example 1 is a film made from ELITE® 5400G, a resin commercially available from the Dow Chemical Company. ELITE 5400G has a density of about 0.916 g/cm³ and a melt index I₂ of about 1 dg/min. Comparative Example 2 is a film made from SURPASS® FP117-C, a resin commercially available from the NOVA Chemicals Corporation. SURPASS FP117-C has a density of 0.917 g/cm³ and a melt index I₂ of 1 dg/min. Comparative Examples 3 and 4 are films made from resins made according to US Pat. Appl. Pub. No. 2016/0108221. Comparative Example 3 is a film made from an ethylene/1-octene copolymer which has a density of about 0.917 g/cm³, a melt index I₂ of about 0.96 dg/min, and which was made in a multi reactor solution process in which a first reactor and a second reactor are configured in series with one another. Comparative Example 4 is a film made from an ethylene/1-octene copolymer which has a density of about 0.913 g/cm³, a melt index I₂ of about 0.85 dg/min, and which was made in a multi reactor solution process in which a first reactor and a second reactor are configured in series with one another. Comparative Example 5 is a film made from SCLAIR® FP112-A, a resin commercially available from the NOVA Chemicals Corporation. SCLAIR FP112-A has a density of 0.912 g/cm³ and a melt index I₂ of 0.9 dg/min. Comparative Example 6 is a film made from EXCEED® 1018CA, a resin commercially available from ExxonMobil. EXCEED 1018CA has a density of about 0.918 g/cm³ and a melt index I₂ of about 0.94 dg/min. Comparative Example 7 is a film made from MARLEX® D139, a resin commercially available from ChevronPhillips. MARLEX D139 has a density of about 0.918 g/cm³ and a melt index I₂ of about 0.9 dg/min. Comparative Example 8 is a film made from SCLAIR® FP120-A, a resin commercially available the NOVA Chemicals Corporation. FP120-A has a density of 0.920 g/cm³ and a melt index I₂ of 1 dg/min. Comparative Example 9 is a film made from SCLAIR® FP026-F, a resin commercially available the NOVA Chemicals Corporation. FP026-F has a density of 0.926 g/cm³ and a melt index I₂ of 0.75 dg/min. In Table 5, the Inventive Examples 1 and 2, are films made from the Inventive polyethylene compositions of Inventive Examples 1 and 2.

TABLE 5 Film Properties Example No. Inventive PE Inventive PE Composition 1 Composition 2 Comparative 1 Comparative 2 Film Physical Properties Thickness Profile Ave 1 1 1.03 1.01 Film Toughness Dart Impact (g/mil) 602 784 818 470 Slow Puncture - Lube/Tef 56 69 63 85 (J/mm) ASTM Puncture (J/mm) 136 165 97 Film Tear Resistance Tear - MD (g/mil) 174 286 247 308 Tear - TD (g/mil) 505 598 485 516 Film Stiffness 1% Sec Modulus - MD 204 216 165 129 (Mpa) 1% Sec Modulus - TD 248 239 175 131.4 (Mpa) 2% Sec Modulus - MD 173 183 151 117 (Mpa) 2% Sec Modulus - TD 209 201 155 123.8 (Mpa) Film Tensile Strength Tensile Break Str - MD 49.4 57.4 44 46.4 (Mpa) Tensile Break Str - TD 40.4 44.2 45.5 48 (Mpa) Elongation at Break - MD 583 513 486 534 (%) Elongation at Break - TD 779 757 725 796 (%) Tensile Yield Str - MD 10.41 10.6 9.1 8.8 (Mpa) Tensile Yield Str - TD 11.5 11.3 8.7 8.8 (Mpa) Tensile Elong at Yield - 10 10 13 22 MD (%) Tensile Elong at Yield - 10 10 13 17 TD (%) Film Opticals Gloss at 45° 32 57 64 50 Haze (%) 19.6 9.7 7.8 12 Cold Seal Properties S.I.T. @ 8.8 N Seal 81.7 94.1 100.4 98.8 Strength (° C.) Max Force (N) 25.1 28 24.9 19.9 Temp. @ Max Force (° C.) 160 160 150 130 Hot Tack Properties Tack Onset @ 1.0 N (° C.) - 63.5 70.5 92.5 100.5 2 mil film Max Hottack Strength (N) - 3.28 4.3 5.4 4.1 2 mil film Temperature - Max. 120 120 110 115 Hottack (° C.) - 2 mil film AHTW (Newtons · ° C.) 189.1 183.1 140 95.3 OTR (cm³ per 100 inch² per day) 847.4 746.1 — 662.8 Example No. Comparative 3 Comparative 4 Comparative 5 Comparative 6 Comparative 7 Film Physical Properties Thickness Profile Ave 1.04 1 1 1.01 1.03 Film Toughness Dart Impact (g/mil) 812 891 546 827 688 Slow Puncture - Lube/Tef 98 80 77 (J/mm) ASTM Puncture (J/mm) 66 151 84 Film Tear Resistance Tear - MD (g/mil) 293 231 376 241 186 Tear - TD (g/mil) 540 548 580 358 454 Film Stiffness 1% Sec Modulus - MD 150.4 145 113 156.8 177.6 (Mpa) 1% Sec Modulus - TD 167.8 134 111 168.8 185 (Mpa) 2% Sec Modulus - MD 141.4 149 136 150.2 166.4 (Mpa) 2% Sec Modulus - TD 149.2 136 127 161.4 170.2 (Mpa) Film Tensile Strength Tensile Break Str - MD 45.4 51.8 56.4 50.7 47.8 (Mpa) Tensile Break Str - TD 44.6 50.6 53.5 61.1 47.8 (Mpa) Elongation at Break - MD 521 557 479 566 505 (%) Elongation at Break - TD 747 751 761 741 692 (%) Tensile Yield Str - MD 9.1 7.9 8 9.7 10.1 (Mpa) Tensile Yield Str - TD 8.9 7.6 7.7 9.9 9.2 (Mpa) Tensile Elong at Yield - 13 10 16 15 16 MD (%) Tensile Elong at Yield - 14 10 15 14 12 TD (%) Film Opticals Gloss at 45° 72 83.8 67 39 84 Haze (%) 5.8 2.9 6.8 16.2 3.3 Cold Seal Properties S.I.T. @ 8.8 N Seal 98.2 93.5 89.75 102.8 102.4 Strength (° C.) Max Force (N) 23.7 24.4 24.70 20.6 23.4 Temp. @ Max Force (° C.) 160 160 155 140 120 Hot Tack Properties Tack Onset @ 1.0 N (° C.) - 95.4 87 78 101.2 98.6 2 mil film Max Hottack Strength (N) - 4.4 5.1 3.5 5.3 5.7 2 mil film Temperature - Max. 115 105 120 120 120 Hottack (° C.) - 2 mil film AHTW (Newtons · ° C.) 111 151 114 103 103.5 OTR (cm³ per 100 inch² 704.6 771.5 845 552.2 545.1 per day) Comparative 8 Comparative 9 Film Physical Properties Thickness Profile Ave 1 1 (mil) Film Toughness Dart Impact (g/mil) 214 156 Slow Puncture - Lube/Tef 73 25 (J/mm) ASTM Puncture (J/mm) 78.5 78 Film Tear Resistance Tear - MD (g/mil) 384 295 Tear - TD (g/mil) 616 640 Film Stiffness 1% Sec Modulus - MD 193 243 (Mpa) 1% Sec Modulus - TD 197 252 (Mpa) 2% Sec Modulus - MD 176 213 (Mpa) 2% Sec Modulus - TD 179 220 (Mpa) Film Tensile Strength Tensile Break Str - MD 52.6 38.4 (Mpa) Tensile Break Str - TD 42.8 35.8 (Mpa) Elongation at Break - MD 608 707 (%) Elongation at Break - TD 767 729 (%) Tensile Yield Str - MD 10.4 12.7 (Mpa) Tensile Yield Str - TD 10.4 13.2 (Mpa) Tensile Elong at Yield - 10.2 10.5 MD (%) Tensile Elong at Yield - 10.7 13.2 TD (%) Film Opticals Gloss at 45° 61.7 56 Haze (%) 11.8 14.0 Cold Seal Properties S.I.T. @ 8.8 N Seal 107.5 116.0 Strength (° C.) Max Force (N) 26.5 31.9 Temp. @ Max Force (° C.) 150 180 Hot Tack Properties Tack Onset @ 1.0 N (° C.) - 98.75 106.4 2 mil film Max Hottack Strength (N) - 4.16 4.3 2 mil film Temperature - Max. 120 140 Hottack (° C.) - 2 mil film AHTW (Newtons · ° C.) 139.1 28.4 OTR (cm³ per 100 inch² per day) 650.8 382.4

The data provided in Table 5 together with the data in FIGS. 4-8 demonstrate that the inventive polyethylene compositions can be made into film having a good balance of film properties, including good stiffness, good oxygen transmission rates and good sealing properties. For example, and with reference to FIGS. 4-8, the films made from the inventive polyethylene compositions have good hot tack and cold seal performance.

Without wishing to be bound by theory, in the hot tack (or cold seal) profile (seal temperature vs. seal force), good hot tack (or cold seal) performance is indicated by an early (or low) hot tack (or cold seal) initiation temperature, then a relatively high sealing force over a wide range of hot tack seal temperatures. See for example the shape the curves in FIGS. 4 and 5 for Inventive Examples 1 and 2, relative to Comparative Examples 1-7. The shape of the hot tack curves for Inventive Examples 1 and 2, are particularly good and have an early hot tack seal initiation temperature combined by a high sealing force over a wide range of hot tack seal temperatures. In an effort to provide a more quantitatively measurement of this improved hot tack sealing performance, a new parameter, the “area of the hot-tack (strength) window” (the “area of hot tack window” or the “AHTW”) has been defined herein. The AHTW is simply an estimate of the area under the hot tack curve from the hot-tack on-set temperature to the temperature immediately prior to the melting of the specimen. As shown in FIG. 4, the temperature prior to the melting of the specimen was typically at 130° C., but not necessarily at 130° C. As shown in Table 5 and in FIG. 4, the Inventive Examples 1 and 2 each have an AHTW of greater than 160 Newtons·° C., whereas each of the Comparative Examples, 1-7, have an AHTW of less than 160 Newtons·° C.

Good cold seal properties are evidenced by the curves given in FIG. 5 for the Inventive Examples 1 and 2. For comparison, the cold seal properties of Comparative Examples 1-7 are also shown in FIG. 5. From FIG. 5, a person skilled in the art will recognize that the Inventive Examples 1 and 2 each have an early cold seal initiation temperature in combination with a relatively high seal force over a wide range of cold seal temperatures. In contrast, the Comparative Examples, 1-7 have a later cold seal initiation temperature, with a narrower range of cold seal temperatures over which a relatively high seal force occurs.

FIG. 6 shows that the Inventive Examples 1 and 2, have a better balance of AHTW and stiffness (as determined by the machine direction (MD) secant modulus at 1% strain) than do the Comparative Examples 2-9. Indeed, FIG. 6, which plots the AHTW (in Newtons·° C.) values (the y-axis) against the machine direction (MD) secant modulus at 1% strain (in MPa) values (the x-axis), along with plot of the equation: AHTW=−2.0981 (machine direction (MD) 1% secant modulus)+564.28, shows that the Inventive Examples 1 and 2 satisfy the condition: AHTW>−2.0981 (machine direction (MD) 1% secant modulus)+564.28, whereas the Comparative Examples 2-9 do not.

FIG. 7, shows that the Inventive Examples 1 and 2, have a better balance of SIT and stiffness (as determined by the machine direction (MD) secant modulus at 1% strain) than do the Comparative Examples 2-9. FIG. 7, which plots the SIT (in ° C.) values (the y-axis) against the machine direction (MD) secant modulus at 1% strain (in MPa) values (the x-axis), along with plot of the equation: SIT=0.366 (machine direction (MD) 1% secant modulus)+22.509, shows that the Inventive Examples 1 and 2 satisfy the condition: SIT<0.366 (machine direction (MD) 1% secant modulus)+22.509, whereas the Comparative Examples 2-9 do not.

FIG. 8, shows that the Inventive Examples 1 and 2, have a better balance of OTR and stiffness (as determined by the machine direction (MD) secant modulus at 1% strain) than do the Comparative Examples 2-9. FIG. 8, which plots the OTR (in cm³ per 100 inch² per day) values (the y-axis) against the machine direction (MD) secant modulus at 1% strain (in MPa) values (the x-axis), along with plot of the equation: OTR=−5.4297 (machine direction (MD) 1% secant modulus)+1767.8, shows that the Inventive Examples 1 and 2 satisfy the condition:

OTR ≥−5.4297 (machine direction (MD) 1% secant modulus)+1767.8, whereas the Comparative Examples 2-9 do not.

Non-limiting embodiments of the present disclosure include the following:

Embodiment A

A polyethylene composition comprising:

from 5 to 80 wt % of a first polyethylene which is an ethylene copolymer, the first polyethylene having a weight average molecular weight M_(w) of from 70,000 to 250,000, a molecular weight distribution M_(w)/M_(n) of <2.3 and from 5 to 100 short chain branches per thousand carbon atoms;

-   -   from 5 to 80 wt % of a second polyethylene which is an ethylene         copolymer or an ethylene homopolymer, the second polyethylene         having a weight average molecular weight M_(w) of from 15,000 to         100,000, a molecular weight distribution M_(w)/M_(n) of <2.3 and         from 0 to 20 short chain branches per thousand carbon atoms; and

from 5 to 80 wt % of a third polyethylene which is an ethylene copolymer or an ethylene homopolymer, the third polyethylene having a weight average molecular weight M_(w) of from 70,000 to 250,000, a molecular weight distribution M_(w)/M_(n) of ≥2.3 and from 0 to 50 short chain branches per thousand carbon atoms; wherein

the number of short chain branches per thousand carbon atoms in first polyethylene (SCB_(PE-1)) is greater than the number of short chain branches per thousand carbon atoms in the second polyethylene (SCB_(PE-2)) and the third polyethylene (SCB_(PE-3));

the number of short chain branches per thousand carbon atoms in the third polyethylene (SCB_(PE-3)) is greater than the number of short chain branches per thousand carbon atoms in the second polyethylene (SCB_(PE-2)); and

the weight average molecular weight of the second polyethylene is less than the weight average molecular weight of the first polyethylene and the third polyethylene; wherein,

the polyethylene composition has a density of ≤0.939 g/cm³, a melt index I₂ of from 0.1 to 10 dg/min, a melt flow ratio, I₂₁/I₂ of ≤40 and has a soluble fraction in a crystallization elution fractionation (CEF) analysis of at least 10 weight percent.

Embodiment B

The polyethylene composition of Embodiment A wherein the polyethylene composition has a unimodal profile in a gel permeation chromatograph (GPC).

Embodiment C

The polyethylene composition of Embodiment A or B wherein the polyethylene composition has a soluble fraction in a crystallization elution fractionation (CEF) analysis of at least 15 weight percent.

Embodiment D

The polyethylene composition of Embodiment A, B or C wherein the polyethylene composition has a melting peak temperature in a differential scanning calorimetry (DSC) analysis at above 125° C.

Embodiment E

The polyethylene composition of Embodiment A, B, C or D wherein the first polyethylene has from 30 to 75 short chain branches per thousand carbon atoms.

Embodiment F

The polyethylene composition of Embodiment A, B, C, D or E wherein the second polyethylene is an ethylene homopolymer.

Embodiment G

The polyethylene composition of Embodiment A, B, C, D, E or F wherein the third polyethylene is an ethylene copolymer and has from 5 to 30 short chain branches per thousand carbon atoms.

Embodiment H

The polyethylene composition of Embodiment A, B, C, D, E, F or G wherein the first polyethylene has a weight average molecular weight, M_(w) of from 75,000 to 200,000.

Embodiment I

The polyethylene composition of Embodiment A, B, C, D, E, F, G or H wherein the second polyethylene has a weight average molecular weight, M_(w) of from 25,000 to 75,000.

Embodiment J

The polyethylene composition of Embodiment A, B, C, D, E, F, G, H or I wherein the third polyethylene has a weight average molecular weight, M_(w) of from 80,000 to 200,000.

Embodiment K

The polyethylene composition of Embodiment A, B, C, D, E, F, G, H, I or J wherein the first polyethylene has a density of from 0.855 to 0.910 g/cm³.

Embodiment L

The polyethylene composition of Embodiment A, B, C, D, E, F, G, H, I, J or K wherein the second polyethylene is an ethylene homopolymer having a density of from 0.940 to 0.980 g/cm³.

Embodiment M

The polyethylene composition of Embodiment A, B, C, D, E, F, G, H, I, J, K or L wherein the third polyethylene is an ethylene copolymer having a density of from 0.880 to 0.936 g/cm³.

Embodiment N

The polyethylene composition of Embodiment A, B, C, D, E, F, G, H, I, J, K, L or M wherein the first polyethylene is present in from 5 to 50 wt %.

Embodiment O

The polyethylene composition of Embodiment A, B, C, D, E, F, G, H, I, J, K, L, M or N wherein the second polyethylene is present in from 5 to 60 wt %.

Embodiment P

The polyethylene composition of Embodiment A, B, C, D, E, F, G, H, I, J, K, L, M, N or O wherein the third polyethylene is present in from 15 to 85 wt %.

Embodiment Q

The polyethylene composition of Embodiment A, B, C, D, E, F, G, H, I, J, K, L or M wherein the first polyethylene is present in from 10 to 40 wt %.

Embodiment R

The polyethylene composition of Embodiment A, B, C, D, E, F, G, H, I, J, K, L, M or Q wherein the second polyethylene is present in from 15 to 45 wt %.

Embodiment S

The polyethylene composition of Embodiment A, B, C, D, E, F, G, H, I, J, K, L, M, Q or R wherein the third polyethylene is present in from 20 to 80 wt %.

Embodiment T

The polyethylene composition of Embodiment A, B, C, D, E, F, G, H, I, J, K, L, M, N, O, P, Q, R or S wherein the first polyethylene has a CDBI₅₀ of at least 75 wt %.

Embodiment U

The polyethylene composition of Embodiment A, B, C, D, E, F, G, H, I, J, K, L, M, N, O, P, Q, R, S or T wherein the third polyethylene is a copolymer with a CDBI₅₀ of less than 75 wt %.

Embodiment V

The polyethylene composition of Embodiment A, B, C, D, E, F, G, H, I, J, K, L, M, N, O, P, Q, R, S, T or U wherein the first polyethylene is a homogeneously branched ethylene copolymer.

Embodiment W

The polyethylene composition of Embodiment A, B, C, D, E, F, G, H, I, J, K, L, M, N, O, P, Q, R, S, T, U or V wherein the third polyethylene is a heterogeneously branched ethylene copolymer.

Embodiment X

The polyethylene composition of Embodiment A, B, C, D, E, F, G, H, I, J, K, L, M, N, O, P, Q, R, S, T, U, V or W wherein the first polyethylene is a made with a single site catalyst.

Embodiment Y

The polyethylene composition of Embodiment A, B, C, D, E, F, G, H, I, J, K, L, M, N, O, P, Q, R, S, T, U, V, W or X wherein the second polyethylene is made with a single site catalyst.

Embodiment Z

The polyethylene composition of Embodiment A, B, C, D, E, F, G, H, I, J, K, L, M, N, O, P, Q, R, S, T, U, V, W, X or Y wherein the third polyethylene is made with a Ziegler-Natta catalyst.

Embodiment AA

The polyethylene composition of Embodiment A, B, C, D, E, F, G, H, I, J, K, L, M, N, O, P, Q, R, S, T, U, V, W, X, Y or Z wherein the polyethylene composition has a molecular weight distribution M_(w)/M_(n) of from 2.1 to 5.5.

Embodiment BB

The polyethylene composition of Embodiment A, B, C, D, E, F, G, H, I, J, K, L, M, N, O, P, Q, R, S, T, U, V, W, X, Y or Z wherein the polyethylene composition has a molecular weight distribution M_(w)/M_(n) of from 2.1 to 4.5.

Embodiment CC

The polyethylene composition of Embodiment A, B, C, D, E, F, G, H, I, J, K, L, M, N, O, P, Q, R, S, T, U, V, W, X, Y, Z, AA or BB wherein the polyethylene composition has a density of <0.935 g/cm³.

Embodiment DD

The polyethylene composition of Embodiment A, B, C, D, E, F, G, H, I, J, K, L, M, N, O, P, Q, R, S, T, U, V, W, X, Y, Z, AA or BB wherein the polyethylene composition has a density of from 0.880 to 0.932 g/cm³.

Embodiment EE

The polyethylene composition of Embodiment A, B, C, D, E, F, G, H, I, J, K, L, M, N, O, P, Q, R, S, T, U, V, W, X, Y, Z, AA, BB, CC or DD wherein the polyethylene composition has a melt index, I₂ of from 0.1 to 3.0 dg/min.

Embodiment FF

The polyethylene composition of Embodiment A, B, C, D, E, F, G, H, I, J, K, L, M, N, O, P, Q, R, S, T, U, V, W, X, Y, Z, AA, BB, CC, DD or EE or wherein the polyethylene composition has a M_(Z)/M_(W) of less than 3.0.

Embodiment GG

The polyethylene composition of Embodiment A, B, C, D, E, F, G, H, I, J, K, L, M, N, O, P, Q, R, S, T, U, V, W, X, Y, Z, AA, BB, CC, DD, EE or FF wherein the polyethylene composition has a melt index ratio, I₂₁/I₂ of from 20 to 40.

Embodiment HH

A film layer having a thickness of from 0.5 to 10 mil, comprising the polyethylene composition of Embodiment A, B, C, D, E, F, G, H, I, J, K, L, M, N, O, P, Q, R, S, T, U, V, W, X, Y, Z, AA, BB, CC, DD, EE, FF or GG.

Embodiment II

The film layer of Embodiment HH wherein the film layer has a machine direction (MD) 1% secant modulus of ≥190 MPa when measured at a film thickness of about 1 mil.

Embodiment JJ

The film layer of Embodiment HH or II wherein the film layer has a seal initiation temperature (SIT) of ≤100° C. when measured at a film thickness of about 2 mil.

Embodiment KK

The film layer of Embodiment HH, II or JJ wherein the film layer has an area of hot tack window (AHTW) of ≥160 Newtons·° C. when measured at a film thickness of about 2 mil.

Embodiment LL

The film layer of Embodiment HH, II, JJ or KK wherein the film layer has an oxygen transmission rate (OTR) of ≥650 cm³ per 100 inch² per day when measured at a film thickness of about 1 mil.

Embodiment MM

The film layer of Embodiment HH wherein the film layer has a machine direction (MD) 1% secant modulus of ≥190 MPa when measured at a film thickness of about 1 mil, a seal initiation temperature (SIT) of ≤100° C. when measured at a film thickness of about 2 mil, an area of hot tack window (AHTW) of ≥160 Newtons·° C. when measured at a film thickness of about 2 mil, and an oxygen transmission rate (OTR) of ≥650 cm³ per 100 inch² per day when measured at a film thickness of about 1 mil.

Embodiment NN

A film layer having a thickness of from 0.5 to 10 mil, wherein the film layer has a machine direction (MD) 1% secant modulus of ≤190 MPa when measured at a film thickness of about 1 mil and a seal initiation temperature (SIT) of ≤100° C. when measured at a film thickness of about 2 mil.

Embodiment OO

A film layer having a thickness of from 0.5 to 10 mil, wherein the film layer has a has a machine direction (MD) 1% secant modulus of −190 MPa when measured at a film thickness of about 1 mil and an area of hot tack window (AHTW) of ≤160 Newtons·° C. when measured at a film thickness of about 2 mil.

Embodiment PP

A film layer having a thickness of from 0.5 to 10 mil, wherein the film layer has a has a machine direction (MD) 1% secant modulus of ≥190 MPa when measured at a film thickness of about 1 mil and an oxygen transmission rate (OTR) of ≥650 cm³ per 100 inch² per day when measured at a film thickness of about 1 mil.

Embodiment QQ

A film layer having a thickness of from 0.5 to 10 mil, wherein the film layer has a has a machine direction (MD) 1% secant modulus of ≥190 MPa when measured at a film thickness of about 1 mil, an oxygen transmission rate (OTR) of ≥650 cm³ per 100 inch² per day when measured at a film thickness of about 1 mil, a seal initiation temperature (SIT) of ≤100° C. when measured at a film thickness of about 2 mil, and an area of hot tack window (AHTW) of ≥160 Newtons·° C. when measured at a film thickness of about 2 mil.

Embodiment RR

Film comprising the polyethylene composition of Embodiment A, B, C, D, E, F, G, H, I, J, K, L, M, N, O, P, Q, R, S, T, U, V, W, X, Y, Z, AA, BB, CC, DD, EE, FF or GG, the film satisfying the following relationship:

area of hot tack window (AHTW)>−2.0981 (machine direction (MD) 1% secant modulus)+564.28;

-   -   wherein the AHTW is measured at a film thickness of about 2 mil,         and the machine direction (MD) 1% secant modulus is measured at         a film thickness of about 1 mil.

Embodiment SS

Film comprising the polyethylene composition of Embodiment A, B, C, D, E, F, G, H, I, J, K, L, M, N, O, P, Q, R, S, T, U, V, W, X, Y, Z, AA, BB, CC, DD, EE, FF or GG, the film satisfying the following relationship:

oxygen transmission rate (OTR)>−5.4297 (machine direction (MD) 1% secant modulus)+1767.8;

wherein the OTR is measured at a film thickness of about 1 mil, and the machine direction (MD) 1% secant modulus is measured at a film thickness of about 1 mil.

Embodiment TT

Film comprising the polyethylene composition of Embodiment A, B, C, D, E, F, G, H, I, J, K, L, M, N, O, P, Q, R, S, T, U, V, W, X, Y, Z, AA, BB, CC, DD, EE, FF or GG, the film satisfying the following relationship:

seal initiation temperature (SIT)<0.366 (machine direction (MD) 1% secant modulus)+22.509;

wherein the SIT is measured at a film thickness of about 2 mil, and the machine direction (MD) 1% secant modulus is measured at a film thickness of about 1 mil.

Embodiment UU

Film comprising the polyethylene composition of Embodiment A, B, C, D, E, F, G, H, I, J, K, L, M, N, O, P, Q, R, S, T, U, V, W, X, Y, Z, AA, BB, CC, DD, EE, FF or GG, the film satisfying the following relationships: i) area of hot tack window (AHTW)>−2.0981 (machine direction (MD) 1% secant modulus)+564.28;

wherein the AHTW is measured at a film thickness of about 2 mil, and the machine direction (MD) 1% secant modulus is measured at a film thickness of about 1 mil;

ii) oxygen transmission rate (OTR)>−5.4297 (machine direction (MD) 1% secant modulus)+1767.8;

wherein the OTR is measured at a film thickness of about 1 mil, and the machine direction (MD) 1% secant modulus is measured at a film thickness of about 1 mil; and

iii) seal initiation temperature (SIT)<0.366 (machine direction (MD) 1% secant modulus)+22.509;

-   -   wherein the SIT is measured at a film thickness of about 2 mil,         and the machine direction (MD) 1% secant modulus is measured at         a film thickness of about 

What is claimed is:
 1. A polyethylene composition comprising: from 5 to 80 wt % of a first polyethylene which is an ethylene copolymer, the first polyethylene having a weight average molecular weight Mw of from 70,000 to 250,000, a molecular weight distribution Mw/Mn of <2.3 and from 5 to 100 short chain branches per thousand carbon atoms; from 5 to 80 wt % of a second polyethylene which is an ethylene copolymer or an ethylene homopolymer, the second polyethylene having a weight average molecular weight Mw of from 15,000 to 100,000, a molecular weight distribution Mw/Mn of <2.3 and from 0 to 20 short chain branches per thousand carbon atoms; and from 5 to 80 wt % of a third polyethylene which is an ethylene copolymer or an ethylene homopolymer, the third polyethylene having a weight average molecular weight Mw of from 70,000 to 250,000, a molecular weight distribution Mw/Mn of >2.3 and from 0 to 50 short chain branches per thousand carbon atoms; wherein the number of short chain branches per thousand carbon atoms in the first polyethylene (SCB_(PE-1)) is greater than the number of short chain branches per thousand carbon atoms in the second polyethylene (SCB_(PE-2)) and the third polyethylene (SCB_(PE-3)); the number of short chain branches per thousand carbon atoms in the third polyethylene (SCB_(PE-3)) is greater than the number of short chain branches per thousand carbon atoms in the second polyethylene (SCB_(PE-2)); and the weight average molecular weight of the second polyethylene is less than the weight average molecular weight of the first polyethylene and the third polyethylene; wherein, the polyethylene composition has a density of ≤0.939 g/cm³, a melt index I₂ of from 0.1 to 10 dg/min, a melt flow ratio, I₂₁/I₂ of ≤40 and has a soluble fraction in a crystallization elution fractionation (CEF) analysis of at least 10 weight percent.
 2. The polyethylene composition of claim 1 wherein the polyethylene composition has a unimodal profile in a gel permeation chromatograph (GPC).
 3. The polyethylene composition of claim 1 wherein the polyethylene composition has a soluble fraction in a crystallization elution fractionation (CEF) analysis of at least 15 weight percent.
 4. The polyethylene composition of claim 1 wherein the polyethylene composition has a melting peak temperature in a differential scanning calorimetry (DSC) analysis at above 125° C.
 5. The polyethylene composition of claim 1 wherein the first polyethylene has from 30 to 75 short chain branches per thousand carbon atoms.
 6. The polyethylene composition of claim 1 wherein the second polyethylene is an ethylene homopolymer.
 7. The polyethylene composition of claim 1 wherein the third polyethylene is an ethylene copolymer and has from 5 to 30 short chain branches per thousand carbon atoms.
 8. The polyethylene composition of claim 1 wherein the first polyethylene has a weight average molecular weight, Mw of from 75,000 to 200,000.
 9. The polyethylene composition of claim 1 wherein the second polyethylene has a weight average molecular weight, Mw of from 25,000 to 75,000.
 10. The polyethylene composition of claim 1 wherein the third polyethylene has a weight average molecular weight, Mw of from 80,000 to 200,000.
 11. The polyethylene composition of claim 1 wherein the first polyethylene has a density of from 0.855 to 0.910 g/cm³.
 12. The polyethylene composition of claim 1 wherein the second polyethylene is an ethylene homopolymer having a density of from 0.940 to 0.980 g/cm³.
 13. The polyethylene composition of claim 1 wherein the third polyethylene is an ethylene copolymer having a density of from 0.880 to 0.936 g/cm³.
 14. The polyethylene composition of claim 1 wherein the first polyethylene is present in from 5 to 50 wt. %.
 15. The polyethylene composition of claim 1 wherein the second polyethylene is present in from 5 to 60 wt. %.
 16. The polyethylene composition of claim 1 wherein the third polyethylene is present in from 15 to 85 wt. %.
 17. The polyethylene composition of claim 1 wherein the first polyethylene is present in from 10 to 40 wt. %.
 18. The polyethylene composition of claim 1 wherein the second polyethylene is present in from 15 to 45 wt. %.
 19. The polyethylene composition of claim 1 wherein the third polyethylene is present in from 20 to 80 wt. %.
 20. The polyethylene composition of claim 1 wherein the first polyethylene has a CDBI₅₀ of at least 75 wt. %.
 21. The polyethylene composition of claim 1 wherein the third polyethylene is a copolymer with a CDBI₅₀ of less than 75 wt. %.
 22. The polyethylene composition of claim 1 wherein the first polyethylene is a homogeneously branched ethylene copolymer.
 23. The polyethylene composition of claim 1 wherein the third polyethylene is a heterogeneously branched ethylene copolymer.
 24. The polyethylene composition of claim 1 wherein the first polyethylene is a made with a single site catalyst.
 25. The polyethylene composition of claim 1 wherein the second polyethylene is made with a single site catalyst.
 26. The polyethylene composition of claim 1 wherein the third polyethylene is made with a Ziegler-Natta catalyst.
 27. The polyethylene composition of claim 1 wherein the polyethylene composition has a molecular weight distribution Mw/Mn of from 2.1 to 5.5.
 28. The polyethylene composition of claim 1 wherein the polyethylene composition has a molecular weight distribution Mw/Mn of from 2.1 to 4.5.
 29. The polyethylene composition of claim 1 wherein the polyethylene composition has a density of <0.935 g/cm³.
 30. The polyethylene composition of claim 1 wherein the polyethylene composition has a density of from 0.880 to 0.932 g/cm³.
 31. The polyethylene composition of claim 1 wherein the polyethylene composition has a melt index, I₂ of from 0.1 to 3.0 dg/min.
 32. The polyethylene composition of claim 1 wherein the polyethylene composition has a Mz/Mw of less than 3.0.
 33. The polyethylene composition of claim 1 wherein the polyethylene composition has a melt index ratio, I₂₁/I₂ of from 20 to
 40. 34. A film layer having a thickness of from 0.5 to 10 mil, comprising the polyethylene composition of claim
 1. 35. The film layer of claim 34 wherein the film layer has a machine direction (MD) 1% secant modulus of ≥190 MPa when measured at a film thickness of about 1 mil.
 36. The film layer of claim 34 wherein the film layer has a seal initiation temperature (SIT) of ≤100° C. when measured at a film thickness of about 2 mil.
 37. The film layer of claim 34 wherein the film layer has an area of hot tack window (AHTW) of ≥160 Newtons·° C. when measured at a film thickness of about 2 mil.
 38. The film layer of claim 34 wherein the film layer has an oxygen transmission rate (OTR) of ≥650 cm³ per 100 inch² per day when measured at a film thickness of about 1 mil.
 39. The film layer of claim 34 wherein the film layer has a machine direction (MD) 1% secant modulus of ≥190 MPa when measured at a film thickness of about 1 mil, a seal initiation temperature (SIT) of ≤100° C. when measured at a film thickness of about 2 mil, an area of hot tack window (AHTW) of ≥160 Newtons·° C. when measured at a film thickness of about 2 mil, and an oxygen transmission rate (OTR) of ≥650 cm³ per 100 inch² per day when measured at a film thickness of about 1 mil.
 40. Film comprising the polyethylene composition of claim 1, the film satisfying the following relationship: area of hot tack window (AHTW in Newtons·° C.) ≥−2.0981 (machine direction (MD) 1% secant modulus in MPa)+564.28; wherein the AHTW is measured at a film thickness of about 2 mil, and the machine direction (MD) 1% secant modulus is measured at a film thickness of about 1 mil.
 41. Film comprising the polyethylene composition of claim 1, the film satisfying the following relationship: oxygen transmission rate (OTR in cm³ per 100 inch² per day) ≥−5.4297 (machine direction (MD) 1% secant modulus in MPa)+1767.8; wherein the OTR is measured at a film thickness of about 1 mil, and the machine direction (MD) 1% secant modulus is measured at a film thickness of about 1 mil.
 42. Film comprising the polyethylene composition of claim 1, the film satisfying the following relationship: seal initiation temperature (SIT in ° C.)<0.366 (machine direction (MD) 1% secant modulus in MPa)+22.509; wherein the SIT is measured at a film thickness of about 2 mil, and the machine direction (MD) 1% secant modulus is measured at a film thickness of about 1 mil.
 43. Film comprising the polyethylene composition of claim 1, the film satisfying the following relationships: i) area of hot tack window (AHTW in Newtons·° C.) >−2.0981 (machine direction (MD) 1% secant modulus in MPa)+564.28; wherein the AHTW is measured at a film thickness of about 2 mil, and the machine direction (MD) 1% secant modulus is measured at a film thickness of about 1 mil; ii) oxygen transmission rate (OTR in cm³ per 100 inch² per day) >−5.4297 (machine direction (MD) 1% secant modulus in MPa)+1767.8; wherein the OTR is measured at a film thickness of about 1 mil, and the machine direction (MD) 1% secant modulus is measured at a film thickness of about 1 mil; and iii) seal initiation temperature (SIT in ° C.)<0.366 (machine direction (MD) 1% secant modulus in MPa)+22.509; wherein the SIT is measured at a film thickness of about 2 mil, and the machine direction (MD) 1% secant modulus is measured at a film thickness of about 1 mil. 